A kind of waterborne polyurethane resin containing pyrimidinone structure and its preparation method and application

A water-based polyurethane and pyrimidinone technology is applied in the fields of polymer synthesis technology and intelligent polymer materials to achieve the effects of good mechanical properties and self-healing properties, good emulsion stability and simple operation.

Active Publication Date: 2021-10-19
GUANGZHOU CHEM CO LTD CHINESE ACADEMY OF SCI +2
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the research on self-healing polyurethane materials combined with host-guest interaction and hydrogen bonding is mainly concentrated in the field of traditional solvent-based polyurethanes, Angewandte Chemie (International ed.in English), 2018, 24(33) 5261-5268; so far, Self-healing by host-guest interaction by introducing UPy groups into the main chain and / or end groups of waterborne polyurethane has not been reported yet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of waterborne polyurethane resin containing pyrimidinone structure and its preparation method and application
  • A kind of waterborne polyurethane resin containing pyrimidinone structure and its preparation method and application
  • A kind of waterborne polyurethane resin containing pyrimidinone structure and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A kind of preparation method of the waterborne polyurethane resin containing pyrimidinone structure, the steps are as follows:

[0040] (1) Polycarbonate diol 2000 and dimethylol propionic acid were distilled under reduced pressure for 2.0 h at 110° C. and a vacuum of 0.080 MPa to remove moisture;

[0041] Add 5.10g of polycarbonate diol 2000 that has been dried and dehydrated, 0.55g of dimethylol propionic acid that has been dried and dehydrated, 2.90g of dicyclohexylmethane diisocyanate, 0.008g of dibutyltin dilaurate into a four-neck flask After stirring, the temperature was raised to 85°C for 3.0 hours to obtain the first prepolymer;

[0042] (2) Cool the obtained first prepolymer to 50°C, add 0.2g UPy, heat up to 85°C and continue the reaction for 2.0h; then cool down to 50°C, add 0.65g of methylated β-cyclodextrin, and heat up to 65°C Continue to react at ℃ for 4h to obtain the second prepolymer;

[0043] (3) Cool the obtained second prepolymer to 35° C., add 2....

Embodiment 2

[0047] A kind of preparation method of the waterborne polyurethane resin containing pyrimidinone structure, the steps are as follows:

[0048] (1) Polycaprolactone diol 2000 and dimethylolpropionic acid were distilled under reduced pressure for 2.0 h at 120°C and a vacuum of 0.070 MPa to remove moisture;

[0049] Add 5.10g of polycaprolactone diol 2000 that has been dried and dehydrated, 0.55g of dimethylol propionic acid that has been dried and dehydrated, 2.46g of dicyclohexylmethane diisocyanate, 0.008g of dilauric acid diisocyanate into a four-neck flask After butyltin was stirred, the temperature was raised to 85°C for 3.0 hours to obtain the first prepolymer;

[0050] (2) Cool the obtained first prepolymer to 50°C, add 0.2g UPy, heat up to 85°C and continue the reaction for 2.0h; then cool down to 50°C, add 0.65g of methylated β-cyclodextrin, and heat up to 65°C Continue to react at ℃ for 4h to obtain the second prepolymer;

[0051] (3) Cool the obtained second prepoly...

Embodiment 3

[0054] A kind of preparation method of the waterborne polyurethane resin containing pyrimidinone structure, the steps are as follows:

[0055] (1) Distill polytetrahydrofuran ether glycol 2000 and dimethylol propionic acid under reduced pressure for 2.0 hours at 120°C and a vacuum of 0.090 MPa to remove moisture;

[0056] Add 2.55g of polytetrahydrofuran ether glycol 2000, 0.55g of dried and dehydrated dimethylol propionic acid, 1.86g of hexamethylene diisocyanate, 0.008g of dibutyltin dilaurate to the four-necked flask After stirring, the temperature was raised to 85°C for 3.0 hours to obtain the first prepolymer;

[0057] (2) Cool the obtained first prepolymer to 50°C, add 0.2g UPy, heat up to 85°C and continue the reaction for 2.0h; then cool down to 50°C, add 0.65g of methylated β-cyclodextrin, and heat up to 65°C Continue to react at ℃ for 4h to obtain the second prepolymer;

[0058] (3) Cool down to 35°C, add 2.5g of acetone to adjust the viscosity of the system, and a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waterborne polyurethane resin containing a pyrimidone structure, a preparation method and application thereof. The method comprises the following steps: heating the macromolecular diol to remove water, then reacting with diisocyanate and a hydrophilic chain extender under stirring and catalytic conditions to obtain a first prepolymer, and combining it with 2-amino- 4-hydroxy-6-methylpyrimidinone diol and cross-linking agent methylated β-cyclodextrin react to obtain the second prepolymer; adjust its viscosity and react with neutralizing agent, then add water and diamine to expand Chain agent, dispersed and emulsified under high-speed stirring to obtain water-based supramolecular polyurethane emulsion. The water-based polyurethane resin containing pyrimidinone structure provided by the present invention exhibits good mechanical properties and self-repairing properties, and the emulsion is transparent with good blue light stability, which is green and environmentally friendly. It can realize self-repairing function under heating conditions, no catalyst is needed, and the operation is simple , high self-healing efficiency; suitable for the preparation of coatings, adhesives, smart textiles and plasticizers.

Description

technical field [0001] The invention belongs to the field of polymer synthesis technology and intelligent polymer materials, and specifically relates to a water-based polyurethane resin containing a pyrimidinone structure and a preparation method and application thereof. Background technique [0002] As one of the important factors affecting the life of polymers, the damage of polymer materials has received more and more attention. Use self-healing materials to solve the inevitable damage problem of polymer materials in actual use, so as to prolong the service life of materials. According to whether a repair agent is added to the polymer matrix, self-healing polymer materials are usually divided into two categories: extrinsic type and intrinsic type. The former mainly includes active healing agents composed of microcapsules and liquid core fibers to enable the material to realize the self-healing function. White and his colleagues report for the first time an extrinsic sel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/66C08G18/64C08G18/44C08G18/42C08G18/48C08G18/12C08G18/34C08G18/32
CPCC08G18/12C08G18/348C08G18/4277C08G18/44C08G18/4854C08G18/6484C08G18/6659C08G18/6692C08G18/3848C08G18/64C08G18/3228
Inventor 史珺肖璐琪黄晓梅姚鸣峰张恩丁吴昆
Owner GUANGZHOU CHEM CO LTD CHINESE ACADEMY OF SCI