Lithium iron phosphate water-based positive electrode slurry and preparation method thereof
A technology of lithium iron phosphate and positive electrode slurry, applied in the field of lithium ion batteries, can solve the problems of difficulty in dispersing lithium iron phosphate, increased difficulty in coating process, easy delamination of slurry, etc. The effect of high efficiency and improved electrical conductivity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0029] Example 1:
[0030] S1: Preparation of composite glue: 3% of the adhesive and part of deionized water are added to the No. 1 mixing tank and stirred at low speed for 30 minutes to prepare composite glue, where the stirring speed is 800 rpm / min;
[0031] S2: Preparation of conductive dispersion: add 0.5% dispersant and part of deionized water to the No. 2 mixing tank and stir at 1000rpm / min for 20min, then add 2% conductive agent in batches at 1800rpm / min Stir at a speed of 60 minutes to prepare a conductive agent dispersion;
[0032] S3: Preparation of lithium iron phosphate dispersion: add 1% dispersant and part of deionized water to the No. 3 agitator and stir at 1000 rpm / min for 20 minutes, then add 47% lithium iron phosphate in batches at 1800 rpm Stir at a speed of 120 min / min to prepare a lithium iron phosphate dispersion;
[0033] S4: One-time mixing and dispersion: Add the conductive agent dispersion prepared by S2 to S1, stir at high speed for 90 minutes to prepare a ...
Example Embodiment
[0036] Example 2:
[0037] S1: Preparation of composite glue: add 4% of the adhesive and part of deionized water to the No. 1 mixing tank and stir at low speed for 30 minutes to prepare composite glue, where the stirring speed is 800 rpm / min;
[0038] S2: Preparation of conductive dispersion: Add 0.7% dispersant and part of deionized water to the No. 2 mixing tank and stir at 1000rpm / min for 20min, then add 3% conductive agent in batches at 1800rpm / min Stir at a speed of 60 minutes to prepare a conductive agent dispersion;
[0039] S3: Preparation of lithium iron phosphate dispersion: add 1% dispersant and part of deionized water to No. 3 agitating tank and stir at 1000rpm / min for 20min, then add 45% lithium iron phosphate in batches at 1800rpm Stir at a speed of 120 min / min to prepare a lithium iron phosphate dispersion;
[0040] S4: One-time mixing and dispersion: Add the conductive agent dispersion prepared by S2 to S1, stir at high speed for 90 minutes to prepare a conductive glu...
Example Embodiment
[0043] Example 3:
[0044] S1: Preparation of composite glue solution: add 2.5% of the adhesive and part of deionized water to the No. 1 mixing tank and stir at low speed for 30 minutes to prepare the composite glue solution, where the stirring speed is 800 rpm / min;
[0045] S2: Preparation of conductive dispersion: add 1% dispersant and part of deionized water to the No. 2 agitator and stir at 1000rpm / min for 20min, then add 4% conductive agent in batches at 1800rpm / min Stir at a speed of 60 minutes to prepare a conductive agent dispersion;
[0046] S3: Preparation of lithium iron phosphate dispersion: add 1% dispersant and part of deionized water to No. 3 agitating tank and stir at 1000rpm / min for 20min, and then add 50% lithium iron phosphate in batches at 1800rpm Stir at a speed of 120 min / min to prepare a lithium iron phosphate dispersion;
[0047] S4: One-time mixing and dispersion: Add the conductive agent dispersion prepared by S2 to S1, stir at high speed for 90 minutes to p...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap