Hot-dip aluminum zinc plate chromate-free passivation solution and preparation method of hot-dip aluminum zinc fingerprint resistant plate
A hot-dip aluminum-zinc plate, chromium-free passivation technology, applied in the direction of metal material coating process, etc. The environmental protection problems of steel plates are outstanding, and the effects of excellent corrosion resistance, good environmental protection and good stability are achieved.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0028] The preparation method of chromium-free passivation solution for hot-dip aluminum-zinc plate, firstly dissolve the zirconium-containing compound in water, then add the corrosion inhibitor, add the rare earth compound after being dissolved, add the water-based organic emulsion and water-based polyurethane emulsion after completely dissolving, and stir evenly Then add the silane coupling agent and stir evenly.
[0029] The invention further discloses a preparation method of a hot-dip galvanized anti-fingerprint plate, which comprises coating the above-mentioned chromium-free passivation solution on the surface of the hot-dip galvalume plate, and then drying and curing to obtain a hot-dip galvanized anti-fingerprint plate.
[0030] Wherein, the curing temperature is 70-100°C, and the curing time is ≥10s.
[0031] In the present invention, there is no special limitation on the hot-dip galvanized sheet. As preferred, the coating chemical composition of the hot-dip galvanized...
Embodiment 6
[0042] In Example 6, the difference from Example 1 is that the zirconium-containing compound is calcium fluorozirconate.
Embodiment 7
[0043] In Example 7, different from Example 1, the rare earth compound is lanthanum chloride.
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap