Hydraulic lime and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of hydraulic lime and carbide slag, which is applied in the field of building materials to achieve the effects of rational use of resources, low energy consumption, and good self-healing properties
Active Publication Date: 2020-06-30
SOUTHWEAT UNIV OF SCI & TECH
View PDF1 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, the domestic research on the production of hydraulic lime with calcium carbide slag industrial waste is blank
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
preparation example Construction
[0018] One aspect of the present invention provides a method for preparing hydraulic lime, in an exemplary embodiment of the method for preparing hydraulic lime of the present invention, as figure 1 As shown, the preparation method may include:
[0019] Step S01, preparing raw materials.
[0020] The preparation of raw materials includes calcium carbide slag as the main raw material, and clinker is added according to a certain mass ratio. In order to make hydraulic lime meet its own performance requirements, such as strength, adhesion, water resistance, repairability, etc., the composition of the raw materials must meet the corresponding requirements. Therefore, the preparation of raw materials is particularly important to the preparation of products. The present invention adopts calcium carbide slag as the main raw material and is combined with clinker, which can well meet the composition requirements of hydraulic lime, saves the calcining process, and has a simple producti...
example 1
[0037] Configure hydraulic lime according to 50% of carbide slag and 50% of white cement clinker, and its preparation method includes:
[0038] 1) Carbide slag is dried;
[0039] 2) According to the mass ratio of 50% calcium carbide slag and 50% white cement clinker, batching is carried out;
[0040] 3) After grinding the raw materials for 2 hours, when the 0.2mm sieve residue does not exceed 5%, and the 0.09mm sieve residue does not exceed 15%, hydraulic lime is obtained.
example 2
[0042] Configure hydraulic lime with 75% calcium carbide slag and 25% white cement clinker. The preparation method includes:
[0043] 1) Carbide slag is dried;
[0044] 2) According to the mass ratio of 75% calcium carbide slag and 25% white cement clinker, batching is carried out;
[0045] 3) After grinding the raw materials for 2 hours, when the 0.2mm sieve residue does not exceed 5%, and the 0.09mm sieve residue does not exceed 15%, hydraulic lime is obtained.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
compressive strength
aaaaa
aaaaa
compressive strength
aaaaa
aaaaa
compressive strength
aaaaa
aaaaa
Login to View More
Abstract
The invention provides hydraulic lime and a preparation method thereof. The preparation method comprises the following steps: preparing raw materials, and grinding the prepared raw materials until thescreen residue with the particle size of 0.2 mm is not more than 5% and the screen residue with the particle size of 0.09 mm is not more than 15% to obtain hydraulic lime, wherein the prepared raw materials comprise, by mass, 50%-90% of carbide slag and the balance cement clinker, and the carbide slag comprises, by mass, 75%-95% of calcium oxide, 0%-10% of silicon dioxide, 0%-5% of aluminum oxideand no more than 3% of sulfur trioxide. The preparation method disclosed by the invention has the advantages of short process flow, simplicity in operation, low energy consumption, low production cost, suitability for large-scale production and the like; and the hydraulic lime can be widely applied to the aspects of cultural relic protection, ancient building repair, historical building repair and reinforcement and the like, and has the advantages of good flexibility and constructability, good viscosity and the like.
Description
technical field [0001] The invention belongs to the technical field of building materials, and more specifically relates to a hydraulic lime and a preparation method thereof. Background technique [0002] Hydraulic lime can be used as a building material, and its main characteristics are different from lime and cement. Compared with lime, hydraulic lime has fast setting speed, good cohesiveness, strong adhesion, high water resistance and high mechanical strength; compared with cement, it can make the wall breathable and keep breathing, which is beneficial to the exchange of water vapor , and has good frost resistance and alkali resistance, good flexibility, good machinability, and strong self-repair ability. Since the hardening rate of hydraulic lime is slower than that of cement, the early hydration heat release is lower, thereby avoiding the internal stress caused by rapid solidification, so that it has good toughness. [0003] In foreign countries, hydraulic lime can be...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More