A kind of melt-blown grade polypropylene with ultra-long antibacterial effect and its preparation method and application

A technology of polypropylene and organic antibacterial agents, which is applied in the field of polymer materials, can solve the problems of poor thermal stability of organic antibacterial agents, and achieve the effects of prolonging antibacterial time, good inhibition effect, and improving aging resistance

Active Publication Date: 2021-05-11
BEIJING UNIV OF CHEM TECH +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In order to overcome the problems existing in the prior art, the inventors have studied diligently, by combining inorganic antibacterial agents (including photocatalytic antibacterial agents and far-infrared radiation antibacterial agents) with synthetic organic antibacterial agents, and modifying the surface of inorganic antibacterial agents. It solves the problem of dispersibility, solves the problem of poor thermal stability of organic antibacterial agents from the technical point of view, and melts and blends antibacterial agents with polypropylene, degradation agents, antioxidants, light stabilizers, fillers, etc. to prepare long-acting antibacterial agents. Melt blown grade polypropylene

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of melt-blown grade polypropylene with ultra-long antibacterial effect and its preparation method and application
  • A kind of melt-blown grade polypropylene with ultra-long antibacterial effect and its preparation method and application
  • A kind of melt-blown grade polypropylene with ultra-long antibacterial effect and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0090] S1, modification of inorganic nano antibacterial agent:

[0091] 1) Put the silane coupling agent KH550 into a beaker filled with absolute ethanol, stir and dilute;

[0092] 2) Add nano-titanium dioxide and nano-alumina (1:1) into (1) diluent, and stir thoroughly;

[0093] 3) The liquid prepared in 2) was reacted at 80° C. for 30 minutes, and the precipitate was collected after centrifugation, dried and ground for later use.

[0094] Table 1: Raw material usage table in S1

[0095] raw material KH550 Nano titanium dioxide + nano alumina Absolute ethanol parts by mass phr 10 10 100

[0096] S2, preparation of organic antibacterial agent masterbatch

[0097] Mix 100 parts by weight of melt-blown grade polypropylene, 0.5% by weight of zinc pyrithione, 0.1% by weight of discoloration inhibitor basic zinc carbonate, and 0.1% by weight of antioxidant 1010 in a mixer, Adding into twin-screws for melt blending and extruding, cooling and pelletizin...

Embodiment 2

[0103] Repeat the process of embodiment 1, difference is: the parts by weight of zinc pyrithione is 1% in the organic antibacterial agent masterbatch.

Embodiment 3

[0105] Repeat the process of embodiment 1, difference is: the parts by weight of zinc pyrithione is 3% in the organic antibacterial agent masterbatch.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a melt-blown grade polypropylene and its preparation method and application. The melt-blown grade polypropylene contains a polypropylene matrix and an antibacterial agent composition, and the antibacterial agent composition is selected from organic antibacterial agents and organic modified Sexual inorganic antibacterial agent, wherein, described inorganic antibacterial agent is selected from photocatalytic antibacterial agent and far-infrared radiation type antibacterial agent. The meltblown grade polypropylene is prepared by meltblowing to obtain a meltblown grade polypropylene nonwoven fabric, which can be used in fields such as medical supplies, textiles, medical sterile bandages, medical sheets, and baby diapers. The preparation method does not need to add new equipment or modify existing equipment, and the process is simple and convenient; the long-acting antibacterial melt-blown polypropylene has a good inhibitory effect on Escherichia coli, Staphylococcus aureus, etc., and the 18h antibacterial rate It can reach 99% and above, and the 360h antibacterial rate can reach 99%.

Description

technical field [0001] The invention belongs to the field of polymer materials, in particular to a melt-blown grade polypropylene material, in particular to a melt-blown grade polypropylene with an ultra-long antibacterial effect and its preparation method and application. Background technique [0002] At present, the antibacterial efficiency of the meltblown cloth made of ordinary meltblown polypropylene is only 90% in general, and the antibacterial efficiency is only 3 months long, and the antibacterial efficiency is only about 50% after three months, which leads to the current antibacterial meltblown polypropylene. The propylene material is completely monopolized by foreign products. The antibacterial melt-blown polypropylene material not only ensures the ultra-high fluidity of polypropylene (melt index> 1200g / 10min), but also realizes the excellent antibacterial effect of the melt-blown cloth, and the antibacterial efficiency reaches 95% % and the antibacterial effect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04H1/4291D04H3/007D01D5/08D01F1/10D01F6/46
CPCD01D5/08D01F1/103D01F6/46D04H1/4291D04H3/007D10B2401/13D10B2501/02D10B2501/021D10B2501/04D10B2509/00D10B2509/02D10B2509/026
Inventor 王媛卢咏来田洪池陈文泉张世甲韩吉彬徐雪梅韩丽丽张立群
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com