A preparation method of consumable electrode rod for copper chromium arc smelting

A technology of arc smelting and consumable electrodes, which is applied in the field of metal processing, can solve the problems of increasing arc smelting product defects, reducing product quality consistency, and low density of prefabricated electrode rods, achieving low relative temperature, improving density, Effect of reducing gas content

Active Publication Date: 2021-05-07
SHAANXI SIRUI ADVANCED MATERIALS CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The disadvantages of these two processes for preparing arc melting prefabricated electrodes are that the process time and efficiency are low, and the prepared prefabricated electrode rods have a high gas content, usually the O content is between 600ppm-800ppm, plus the density of the prefabricated electrode rods Low: between 75%-85%, higher gas content and lower electrode rod density will disturb the arc stability during melting, increase the defects of arc melting products, and reduce the consistency of product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of consumable electrode rod for copper chromium arc smelting
  • A preparation method of consumable electrode rod for copper chromium arc smelting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A method for preparing a consumable electrode rod for copper-chromium arc smelting, comprising the following steps:

[0035] (1) Ingredients: by weight percentage, take 60% copper material and 40% chromium material for proportioning; copper material adopts electrolytic copper plate with a purity greater than 99.990%, and chromium material adopts chromium block with a purity greater than 99.9%, electrolytic copper plate and chromium The block is sanded to remove the surface oxide layer before smelting. The advantages of using electrolytic copper plate and chromium block are not easy to be oxidized and surface oxidized components are easy to remove compared with powdered raw materials.

[0036] (2) Ingot casting: the copper material and chromium material taken in proportion in step (1) are smelted and melted into liquid, and then poured into copper-chromium alloy ingot;

[0037] (3) Powder making: the copper-chromium alloy ingot is made into spherical copper-chromium all...

Embodiment 2

[0042] This embodiment is basically the same as that of Embodiment 1, except that, by weight percentage, 52% copper material and 48% chromium material are used for proportioning.

Embodiment 3

[0044] This embodiment is basically the same as that of Embodiment 1, the difference is that, by weight percentage, 90% copper material and 10% chromium material are used for proportioning.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a consumable electrode rod for copper-chromium arc smelting, which belongs to the technical field of metal processing, and includes batching-ingot-making-powder-making-billet-degassing-hot isostatic pressing, wherein the blank-making step In order to select spherical copper-chromium alloy powders with a particle size of 5-15 μm, the copper-chromium alloy billet rods are made of copper-chromium alloy blanks by cold pressing or cold spray deposition, and the hot isostatic pressing process significantly improves the consumable electrode rod. The density of the consumable electrode has been increased from 75%-85% to about 99%, which is conducive to improving the arc stability of the consumable electrode rod during the smelting process, and also significantly reduced the gas content of the consumable electrode rod. The 600‑800ppm is reduced to 210‑400ppm, which reduces the voltage fluctuation in the electrode rod melting procedure.

Description

technical field [0001] The invention belongs to the technical field of metal processing, and in particular relates to a preparation method of a consumable electrode rod for copper-chromium arc melting. Background technique [0002] Vacuum copper-chromium series electrical contact materials are widely used in the field of medium-voltage series vacuum interrupters due to their excellent arc extinguishing, anti-welding resistance and arc ablation resistance. At present, the mainstream processes for preparing this contact material include: Vacuum infiltration, powder metallurgy, vacuum induction smelting and arc smelting processes, among which the copper chromium series contact materials prepared by the arc smelting process have the advantages of uniformly distributed microstructure, low gas content, and good product quality consistency, etc., but The cost of this process is high, the main factors are: the arc melting equipment is expensive and the process of preparing the prefa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C9/00C22C1/04C22C1/02C22F1/08C23C24/08B22F9/08B22F3/24B22F3/15B22F3/04C22B9/20
CPCB22F3/04B22F3/15B22F3/24B22F9/082B22F2003/248B22F2998/10C22B9/20C22C1/02C22C1/0425C22C9/00C22F1/002C22F1/08C23C24/087Y02P10/25
Inventor 李鹏王文斌刘凯张石松王小军杨斌李刚师晓云赵俊
Owner SHAANXI SIRUI ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com