A deodorant material

A kind of amine odor and solution technology, applied in the field of amine odor removal materials, can solve the problems of activated carbon pore collapse, pore structure regulation, etc., and achieve the effect of superior loading effect

Active Publication Date: 2022-07-05
QINGDAO HSJ ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Patent No. CN 104368307 A, titled "A preparation method of special activated carbon for ammonia adsorption", patent No. CN109455713 A, titled "Preparation process of industrial high-efficiency deamination activated carbon", patent No. CN107952413 A, titled "Modified high-efficiency ammonia-resistant activated carbon and preparation method” all use activated carbon as the base material and acid as the modifying agent to prepare the ammonia gas removal material, but none of the above-mentioned technical solutions stipulates the pore structure of the base material, and because the basic group of the activated carbon itself More, during the acid modification process, the basic groups in the activated carbon will be neutralized first, causing some pores of the activated carbon to collapse

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A kind of deodorant material, its preparation method comprises the steps:

[0038] (1) choose the spherical zeolite of 1-3mm as the base material of adsorption material, carry out hydrothermal treatment to the spherical zeolite in the reactor with 5% ammonia solution, namely the speed of feeding into the furnace after the atomization of the ammonia solution is 6ml / min, The heating rate of the furnace body is 5 °C / min, the temperature is raised to 250 °C, and the temperature is kept for 2 hours. After cooling with the furnace, it is washed three times with clean water and dried in a 100 °C oven to obtain the modified material carrier.

[0039] The specific surface area of ​​spherical zeolite increased from 320㎡ / g to 397㎡ / g before and after the test treatment.

[0040] (2) The above modified material carrier is dipped in a phosphoric acid solution with a mass fraction of 2% for 60 minutes, and then dried at 100° C. to obtain an impregnated carrier.

[0041] (3) Impregnat...

Embodiment 2

[0044] A kind of deodorant material, its preparation method comprises the steps:

[0045] (1) Select the spherical porous resin of 1-3 mm as the base material of the adsorption material, and perform hydrothermal treatment on the spherical porous resin in the reactor with 15% ammonium chloride solution, that is, the ammonium chloride solution is atomized and passed into the furnace. The speed is 7ml / min, the heating rate of the furnace body is 5°C / min, the temperature is raised to 300°C, and the temperature is kept for 2h. After cooling with the furnace, it is washed three times with clean water and dried in a 100°C oven to obtain the modified material carrier.

[0046] The specific surface area of ​​the spherical porous resin increased from 576㎡ / g to 612㎡ / g before and after the test treatment.

[0047] (2) The above modified material carrier is immersed in an acetic acid solution with a mass fraction of 2.5% for 90 minutes, and then dried at 120° C. to obtain an impregnated ca...

Embodiment 3

[0051] A kind of deodorant material, its preparation method comprises the steps:

[0052] (1) Select 1-3mm silicon balls (porous silica) as the substrate of the adsorption material, and perform hydrothermal treatment on the silicon balls in the reactor with 7% ammonium dihydrogen phosphate solution, that is, atomization of the ammonium dihydrogen phosphate solution The speed of passing into the furnace is 5ml / min, the heating rate of the furnace body is 5℃ / min, the temperature is raised to 350℃, and the temperature is kept for 4h. A modified material carrier is obtained.

[0053] The specific surface area of ​​the silicon spheres before and after the test treatment increased from 340㎡ / g to 420㎡ / g.

[0054] (2) The above modified material carrier is immersed in an acetic acid solution with a mass fraction of 1% for 30 minutes, and then dried at 100° C. to obtain an impregnated carrier.

[0055] (3) Impregnating the impregnated carrier into a mixed solution of 0.6 mol / L cerium...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention provides an amine deodorizing material, which belongs to the field of deodorizing materials. The preparation method includes the following steps: (1) hydrothermally treating the adsorption material in the reactor with an inorganic salt solution, cleaning and drying to obtain a modified material carrier; (2) placing the modified material carrier in an acidic solution After impregnation, drying is performed to obtain an impregnated carrier; (3) a catalytically active precursor solution is configured, and the impregnated carrier is again immersed in the catalytically active precursor solution in equal volume, and the reaction is kept warm, and then calcined to obtain . The invention can effectively adjust the specific surface area, porosity and average pore size of the selected adsorbent material, can match the loading amount in grades, and the material loading effect is more superior, and then effectively removes various amines at the same time through the synergistic effect of catalysis and adsorption in a normal temperature environment odorous gas.

Description

technical field [0001] The invention relates to the field of deodorizing materials, in particular to an amine deodorizing material. Background technique [0002] With the development of the economy and the improvement of living standards, people's environmental awareness has gradually increased, and odor pollution, as one of the environmental hazards, has received high attention worldwide. Odor pollution mainly includes two types of odors produced in daily life and odors produced in industrial production. The sources of odors in daily life include: odors emitted by interior decoration materials, including paints, adhesives and other odorous gases containing volatile organic compounds that are more toxic to humans; in addition, kitchens, living rooms, toilets, garbage dumps, Pet rooms are places where foul odors often occur. The main sources of malodor in industrial production are: chemical plants, pesticide plants, paint plants, food fermentation plants, poultry plants, et...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/16B01D53/02B01J23/34B01J29/00B01J35/10B01J20/30
CPCB01J20/08B01J20/103B01J20/14B01J20/165B01D53/02B01J23/002B01J23/34B01J29/00B01J35/1019B01J2523/00B01D2257/406B01J2523/3712B01J2523/41B01J2523/72B01J2523/31Y02A50/20
Inventor 秦玲梁鹏韩光涛朱昊迟淑丽万月亮
Owner QINGDAO HSJ ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap