An amine odor and adsorption material technology, applied in the field of amine odor removal materials, can solve the problems of activated carbon pore collapse, pore structure regulation, etc., and achieve the effect of superior load effect

Active Publication Date: 2020-09-04
QINGDAO HSJ ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Patent No. CN 104368307 A, titled "A preparation method of special activated carbon for ammonia adsorption", patent No. CN109455713 A, titled "Preparation process of industrial high-efficiency deamination activated carbon", patent No. CN107952413 A, titled "Modified high-efficiency ammonia-resistant activated carbon and preparation method” all use activated carbon as the base material and acid as the modifying agent to prepare the ammonia gas removal material, but none of the above-mentioned technical solutions stipulates the pore structure of the base material, and because the basic group of the activated carbon itself More, during the acid modification process, the basic groups in the activated carbon will be neutralized first, causing some pores of the activated carbon to collapse

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A kind of amine deodorizing material, its preparation method comprises the steps:

[0038] (1) choose the spherical zeolite of 1-3mm to be the adsorbent material base material, carry out hydrothermal treatment to the spherical zeolite in the reactor with 5% ammonia solution, the speed that passes into the furnace after the ammonia solution atomization is 6ml / min, The heating rate of the furnace body is 5°C / min, the temperature is raised to 250°C, and the temperature is kept for 2 hours. After cooling down with the furnace, it is washed 3 times with clean water and dried in an oven at 100°C to obtain the modified material carrier.

[0039] The specific surface area of ​​spherical zeolite increased from 320㎡ / g to 397㎡ / g before and after the test treatment.

[0040] (2) Immerse the above-mentioned modified material carrier in a phosphoric acid solution with a mass fraction of 2% for 60 minutes, and then dry it at 100° C. to obtain the impregnated carrier.

[0041] (3) Imm...

Embodiment 2

[0044] A kind of amine deodorizing material, its preparation method comprises the steps:

[0045] (1) choose the spherical porous resin of 1-3mm to be the adsorbent material substrate, carry out hydrothermal treatment to the spherical porous resin in the reactor with 15% ammonium chloride solution, i.e. pass into the furnace after the ammonium chloride solution is atomized The speed is 7ml / min, the heating rate of the furnace body is 5°C / min, the temperature is raised to 300°C, and the temperature is kept for 2 hours. After cooling down with the furnace, it is washed with clean water for 3 times and dried in an oven at 100°C to obtain the modified material carrier.

[0046] The specific surface area of ​​the spherical porous resin increased from 576㎡ / g to 612㎡ / g before and after the test treatment.

[0047] (2) Immerse the above-mentioned modified material carrier in an acetic acid solution with a mass fraction of 2.5% for 90 minutes, and then dry it at 120° C. to obtain the i...

Embodiment 3

[0051] A kind of amine deodorizing material, its preparation method comprises the steps:

[0052] (1) Select 1-3mm silicon spheres (porous silica) as the substrate of the adsorption material, and use 7% ammonium dihydrogen phosphate solution to carry out hydrothermal treatment on the silicon spheres in the reactor, that is, the ammonium dihydrogen phosphate solution is atomized Finally, the speed of passing into the furnace is 5ml / min, the heating rate of the furnace body is 5°C / min, the temperature is raised to 350°C, and the temperature is kept for 4 hours. A modified material carrier is obtained.

[0053] The specific surface area of ​​silicon spheres before and after the test treatment increased from 340㎡ / g to 420㎡ / g.

[0054] (2) Immerse the above-mentioned modified material carrier in an acetic acid solution with a mass fraction of 1% for 30 minutes, and then dry it at 100° C. to obtain the impregnated carrier.

[0055] (3) Immerse the equal volume of the impregnated c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention provides an amine odor removal material, and belongs to the field of odor removal materials. The preparation method comprises the following steps: (1) carrying out hydro-thermal treatment on an adsorption material in a reactor by using an inorganic salt solution, and performing cleaning and drying to obtain a modified material carrier; (2) impregnating the modified material carrier in an acidic solution, and drying the modified material carrier to obtain an impregnated carrier; and (3) preparing a catalytic active precursor solution, impregnating the impregnated carrier into thecatalytic active precursor solution again in an isopyknic manner, carrying out heat preservation reaction, and then performing roasting to obtain the material. According to the invention, the specificsurface area, porosity and average pore size of the selected adsorption material can be effectively adjusted, the graded loading capacity can be realized, the material loading effect is more excellent, and various amine malodorous gases can be effectively removed at the same time through the synergistic effect of catalysis and adsorption in a normal-temperature environment.

Description

technical field [0001] The invention relates to the field of deodorizing materials, in particular to an amine deodorizing material. Background technique [0002] With the development of the economy and the improvement of living standards, people's awareness of the environment has gradually increased. As one of the environmental hazards, odor pollution has attracted great attention worldwide. Odor pollution mainly includes two types of odors generated in daily life and odors generated in industrial production. The sources of stench in daily life include: the stench emitted by interior decoration materials, including paints, adhesives and other stench gases containing volatile organic compounds that are more poisonous to the human body; Pet rooms are places where bad odors often occur. Odor sources in industrial production mainly include: chemical plants, pesticide plants, paint plants, food fermentation plants, poultry plants, etc. These malodorous gases mainly include vol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/16B01D53/02B01J23/34B01J29/00B01J35/10B01J20/30
CPCB01J20/08B01J20/103B01J20/14B01J20/165B01D53/02B01J23/002B01J23/34B01J29/00B01J35/1019B01J2523/00B01D2257/406B01J2523/3712B01J2523/41B01J2523/72B01J2523/31Y02A50/20
Inventor 秦玲梁鹏韩光涛朱昊迟淑丽万月亮
Owner QINGDAO HSJ ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap