Environment-friendly hot-melt marking coating and preparation method thereof

A hot-melt marking paint, environmentally friendly technology, applied in the direction of reflection/signal paint, coating, conjugated diene coating, etc., can solve serious, pollution, crack resistance, compressive strength and fluidity performance indicators Substandard and other problems, to achieve the effect of prolonging service life, reducing pollution, acid and alkali resistance and reflective performance

Inactive Publication Date: 2020-09-08
杨三强 +5
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In summary, the current hot-melt marking paint still has the following problems: serious pollution, performance indicators such as crack resistance, compressive strength and fluidity are not up to standard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly hot-melt marking coating and preparation method thereof
  • Environment-friendly hot-melt marking coating and preparation method thereof
  • Environment-friendly hot-melt marking coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0079] The environment-friendly type hot-melt marking paint of the present embodiment is made by the raw material of following weight: modified C5 petroleum resin 13kg, chrome yellow 8kg, quartz sand 27kg, heavy calcium carbonate 28kg, castor oil 1kg, polyethylene wax 4kg, Powdered nitrile rubber 1kg and glass microspheres 23kg.

[0080] Wherein, the modified C5 petroleum resin is prepared by the following method:

[0081] Step 1.1: Weigh the following raw materials to make: 100kg of C5 petroleum resin, 12kg of maleic anhydride and 17kg of powdered nitrile rubber;

[0082] Step 1.2: heat up the 60% by weight C5 petroleum resin weighed in step 1 to 150° C., feed in nitrogen, stir and melt to obtain a primary stirring liquid;

[0083] Step 1.3: Add the remaining C5 petroleum resin to the primary stirring liquid obtained in step 2, and slowly add the maleic anhydride weighed in step 1 while stirring at 150°C, and stir for 1h-2h to obtain maleic C5 petroleum resin;

[0084] Step...

Embodiment 2

[0096] The environment-friendly hot-melt marking paint of the present embodiment is made of the following raw materials: modified C5 petroleum resin 14kg, pigment 7kg, quartz sand 28kg, heavy calcium carbonate 27kg, castor oil 2kg, polyethylene wax 3kg, powder Nitrile rubber 2kg and glass beads 22kg.

[0097] Wherein, the modified C5 petroleum resin is prepared by the following method:

[0098] Step 1.1: Weigh the following raw materials to make: 100kg of C5 petroleum resin, 13kg of maleic anhydride and 16kg of powdered nitrile rubber;

[0099] Step 1.2: heat up the 62% by weight C5 petroleum resin weighed in step 1 to 152° C., feed in nitrogen, stir and melt to obtain a primary stirring liquid;

[0100] Step 1.3: Add the remaining C5 petroleum resin to the primary stirring liquid obtained in step 2, and slowly add the maleic anhydride weighed in step 1 while stirring at 152°C, and stir for 1.5 hours to obtain maleic C5 petroleum resin;

[0101] Step 1.4: At 198°C, add the p...

Embodiment 3

[0114] The environment-friendly hot-melt marking paint of the present embodiment is made of the following raw materials: modified C5 petroleum resin 15kg, pigment 6kg, quartz sand 29kg, heavy calcium carbonate 26kg, castor oil 3kg, polyethylene wax 2kg, powder Nitrile rubber 3kg and glass beads 20kg.

[0115] Wherein, the modified C5 petroleum resin is prepared by the following method:

[0116] Step 1.1: Weigh the following raw materials to make: 100kg of C5 petroleum resin, 15kg of maleic anhydride and 15kg of powdered nitrile rubber;

[0117] Step 1.2: heat up the 65% by weight C5 petroleum resin weighed in step 1 to 155° C., feed in nitrogen, stir and melt to obtain a primary stirring liquid;

[0118] Step 1.3: Add the remaining C5 petroleum resin to the primary stirring liquid obtained in step 2, and slowly add the maleic anhydride weighed in step 1 while stirring at 155° C., and stir for 2 hours to obtain maleic C5 petroleum resin;

[0119] Step 1.4: At 200°C, add the p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an environment-friendly hot-melt marking coating and a preparation method thereof, and belongs to the technical field of environment-friendly hot-melt marking coatings. The environment-friendly hot-melt marking coating is prepared from, by weight, 13-15 parts of modified C5 petroleum resin, 6-8 parts of a pigment, 27-29 parts of quartz sand, 26-28 parts of ground calcium carbonate, 1-3 parts of castor oil, 2-4 parts of polyethylene wax, 1-3 parts of powdered acrylonitrile-butadiene rubber and 20-23 parts of glass beads. The invention also discloses a preparation methodof the environment-friendly hot-melt marking coating. The environment-friendly hot-melt marking coating has the advantages of good fluidity, high compressive strength, short drying time, high softening point, good flexibility, water resistance, acid and alkali resistance, good light reflection performance and the like.

Description

technical field [0001] The invention relates to an environment-friendly hot-melt marking paint and a preparation method thereof, belonging to the technical field of hot-melt marking paint. Background technique [0002] The road performance of road traffic marking materials not only affects road maintenance and maintenance costs, but also directly affects traffic safety. Road marking paints on the market can usually be divided into two categories: solvent-based and hot-melt. Solvent-based marking paint releases a large amount of solvent during use, pollutes the environment, and the paint film takes a long time to dry and has poor wear resistance, so it usually only lasts for about 3 months. Hot-melt marking paint has the characteristics of excellent durability, quick drying, good visibility at night and no solvent. Therefore, it has received extensive attention since its inception, and its usage has increased year by year. [0003] With the rapid development of road traffic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D157/02C09D123/06C09D109/02C09D7/61C09D7/65C09D7/45C09D5/33
CPCC08K2003/2241C08K2003/265C08L2205/035C09D5/004C09D157/02C09D7/45C09D7/61C09D7/65C09D7/70C08L91/00C08L23/06C08L9/02C08K13/04C08K7/20C08K3/36C08K3/26C08K3/22
Inventor 杨三强马鹏蕊赵柯吉申新蕊穆海峰闪金龙
Owner 杨三强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap