Infrared light excited carbonization auxiliary agent, and preparation method and application thereof

A technology of carbonization additives and infrared light, which is applied in laser welding equipment, manufacturing tools, welding equipment, etc.

Inactive Publication Date: 2020-10-02
ZHONGSHAN YUNHAO TECH CO LTD
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, but in the prior art, the research on its ideal laser marking additive still has the problem of marking contrast and color difference contrast, so it is necessary to develop a laser marking additive that can produce relatively excellent color difference contrast in the process of laser marking

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Infrared light excited carbonization auxiliary agent, and preparation method and application thereof
  • Infrared light excited carbonization auxiliary agent, and preparation method and application thereof
  • Infrared light excited carbonization auxiliary agent, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0058] A second aspect of the present invention provides a method for preparing the infrared light-excited carbonization aid, the steps at least including: (1) blending and melt-extruding metal powder, metal oxide, and semi-aromatic polyamide Granulating to obtain primary mixture particles; (2) Blending, melting, extruding and granulating the primary mixture particles, compatibilizer and carrier resin to obtain the product.

[0059] In some preferred embodiments, the steps of the preparation method of the infrared light-activated carbonization aid include at least: (1) blending, melting, extruding and granulating metal powder, metal oxide, and semi-aromatic polyamide, Obtain primary mixture particles; (2) Blend, melt, extrude and granulate primary mixture particles, compatibilizers and carrier resins to obtain the product.

[0060] In some embodiments, the processing equipment in the steps (1) and (2) is a twin-screw extrusion granulator with a screw diameter of 30 mm.

[006...

Embodiment 1

[0066] An infrared light-excited carbonization aid, the raw materials include at least 0.05 parts of metal powder, 46 parts of metal oxide, 22 parts of semi-aromatic polyamide, 3 parts of compatibilizer and 28 parts of carrier resin in terms of weight percentage.

[0067] The metal powder is aluminum powder, and the average particle size of the metal powder is 5 μm.

[0068] The metal oxide is antimony trioxide, and the average particle size of the antimony trioxide is 0.5 μm.

[0069] The metal oxides also include rare earth oxides; the added amount of the rare earth oxides is 0.2% of the weight of antimony trioxide.

[0070] The rare earth oxide is neodymium oxide, and the average particle diameter of the neodymium oxide is 40nm.

[0071] The semi-aromatic polyamide is a mixture of PA6T and PA12T; the weight ratio of PA6T and PA12T is 1:2. The PA6T and PA12T were purchased from Solvay Investment Co., Ltd.

[0072] The carrier resin is LDPE, the melt flow rate of the LDPE ...

Embodiment 2

[0077] An infrared light-excited carbonization aid, the raw materials include at least 0.03 parts of metal powder, 40 parts of metal oxide, 20 parts of semi-aromatic polyamide, 2.5 parts of compatibilizer and 25 parts of carrier resin in terms of weight percentage.

[0078] The metal powder is aluminum powder, and the average particle diameter of the metal powder is 1 μm.

[0079] The metal oxide is antimony trioxide, and the average particle size of the antimony trioxide is 0.1 μm.

[0080] The metal oxides also include rare earth oxides; the added amount of the rare earth oxides is 0.1% of the weight of antimony trioxide.

[0081] The rare earth oxide is neodymium oxide, and the average particle size of the neodymium oxide is 20nm.

[0082] The semi-aromatic polyamide is a mixture of PA6T and PA12T; the weight ratio of PA6T and PA12T is 1:1. The PA6T and PA12T were purchased from Solvay Investment Co., Ltd.

[0083] The carrier resin is LDPE, the melt flow rate of the LDP...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
melt flow indexaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of infrared light excited carbonization auxiliary agents, and provides an infrared light excited carbonization auxiliary agent. The infrared light excitedcarbonization auxiliary agent at least comprises the following components of, in parts raw material, 0.01-0.15 part of metal powder, 35-55 parts of metal oxide, 15-30 parts of semi-aromatic polyamide,2-4 parts of compatilizer and 20-35 parts of carrier resin. The prepared infrared light excited carbonization auxiliary agent can be suitable for different types of polymer matrix materials, such asPP, PE, PET, PS, PVC, PC and other plastics can form very obvious color contrast, and the infrared light excited carbonization auxiliary agent can not change the color and characteristics of the product, absorb enough laser to raise the local temperature to burn or foam plastic, and improve the identification effect, especially the color difference contrast is the most excellent when the mark is applied to the PP polyolefin resin.

Description

technical field [0001] The present invention relates to the technical field of infrared light-excited carbonization aids, and more specifically relates to an infrared light-excited carbonization aid and its preparation method and application. Background technique [0002] The traditional method of marking on the plastic surface is printing, but the cost is high, it is not environmentally friendly, and it is easy to wipe off. Laser engraving refers to the use of a laser beam to act on the material to cause a change in the shape or performance of the sample. It is a high-power-density spot formed by focusing the laser beam. In a few microseconds, the temperature of the spot area rises to the melting point or even the boiling point of the material. Make the material at the irradiated place melt and vaporize, ablate or reach the ignition point immediately. When the laser beam moves along the set path, the photons interact with the material continuously, and at the same time, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23K26/362B23K26/70
CPCB23K26/362B23K26/702B23K2103/42
Inventor 杨优其
Owner ZHONGSHAN YUNHAO TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products