A technology of alumina and zirconia, applied in the field of cast green co-sintered sheets, can solve the problems of decreased insulation, sintering performance, strength and compatibility mismatch and so on

Active Publication Date: 2020-10-20
镇江锆源传感科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the deficiencies of the prior art, the present invention provides a method for preparing co-sintered sheets of zirconia and alumina tape-cast green bodies, which solves the problems of decreased insulation caused by co-sintering and mismatch of sintering performance, strength and compatibility at the same time. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] The described embodiments are some, but not all, embodiments of the invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0028] A method for preparing a co-sintered sheet of zirconia and alumina tape-cast green body, the tape-cast green co-sintered sheet is formed by tape-cast co-sintering of zirconia tape and alumina composite system, characterized in that: The casting of the zirconia is mixed and ball-milled by zirconia powder, solvent, binder, dispersant, plasticizer and lubricant raw materials in a certain proportion; the casting of the alumina compounding system is made of alumina compounding powder , solvent, binder, dispersant, plasticizer and lubricant raw materials are mixed and ball milled in a certain proportion.

[0029] Preferably, the raw material of the zirconia casting and its components ar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a zirconium oxide and aluminum oxide tape casting green body co-sintered sheet layer. According to the preparation method, enstatite (the main componentis Mg2[Si2O6]Fe2[Si2O6]) is selected; the thermal expansion coefficient of enstatite is 13.5 ppm / k, the addition amount of enstatite is 42%, the addition amount of nano Al2O3 is 58%, the thermal expansion coefficient of enstatite can be consistent with the that of zirconium oxide, and meanwhile, the insulation property, the sintering characteristic, the strength and the compatibility of enstatitecan be matched. The problems that the insulating property is reduced and the sintering property, strength and compatibility are not matched due to co-sintering at present are solved.

Description

technical field [0001] The invention relates to the technical field of co-sintered sheets of tape-cast green bodies, in particular to a preparation method of co-sintered sheets of tape-cast green bodies of zirconia and alumina. Background technique [0002] At present, the chip oxygen sensors for automobiles are all made of zirconia substrates, because various functional units are printed on them and then laminated, and the heating unit is required to be insulated from the signal unit to prevent the temperature from rising. The conduction of the substrate causes the heating signal to interfere with the electrochemical signal. The heating unit needs to be insulated, which is usually carried out by printing the aluminum oxide insulating layer on the upper and lower sides of the heating unit. However, the pins are outside and the heating circuit is inside. They are usually connected through via holes. The insulation treatment of via holes is very difficult. The hole is insulat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/48C04B35/634C04B35/632C04B35/10C04B35/622
CPCC04B35/48C04B35/6342C04B35/632C04B35/63488C04B35/10C04B35/622C04B2235/3427C04B2235/96
Inventor 谢光远邱电荣王晓宁张宇明孙宏伟
Owner 镇江锆源传感科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap