Profiled steel sheet-ardealite-calcium silicate board composite floor and manufacturing method thereof

A technology of profiled steel plate and calcium silicate plate, which is applied to floors, building components, thermal insulation, etc., can solve the problems of dust pollution, landslides and other geological disasters, and the actual utilization rate of phosphogypsum is less than 30%, and improve thermal performance. , Improve fire performance, good energy saving effect

Inactive Publication Date: 2020-12-15
GUIZHOU UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the grim thing is: my country's current stockpile of phosphogypsum has exceeded 500 million tons, and the new stockpiles are 60 million tons every year. The newly increased phosphogypsum needs to occupy about 5,000 hectares of land. The stockpiling of a large amount of phosphogypsum is very

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Profiled steel sheet-ardealite-calcium silicate board composite floor and manufacturing method thereof
  • Profiled steel sheet-ardealite-calcium silicate board composite floor and manufacturing method thereof
  • Profiled steel sheet-ardealite-calcium silicate board composite floor and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] In order to facilitate understanding of the present invention, the present invention will be described more fully hereinafter with reference to the related drawings. The preferred embodiments of the invention are shown in the accompanying drawings. However, the present invention may be embodied in many different forms and is not limited to the embodiments described herein. Rather, these embodiments are provided so that a thorough and complete understanding of the present disclosure is provided.

[0028] In addition, when an element in the present invention is referred to as being "fixed to" or "disposed on" another element, it can be directly on the other element or intervening elements may also be present. When an element is referred to as being "connected" to another element, it can be directly connected to the other element or intervening elements may also be present. The terms "vertical", "horizontal", "left", "right" and similar expressions used herein are for th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a profiled steel sheet-ardealite-calcium silicate board composite floor and a manufacturing method thereof. The manufacturing method comprises the steps that a profiled steel sheet and C-shaped connecting pieces are blanked according to design requirements, and the C-shaped connecting pieces are mounted on the top surface of the profiled steel sheet through self-tapping screws; after all the C-shaped connecting pieces are mounted, the profiled steel sheet with the C-shaped connecting pieces is mounted on a floor beam, and then ardealite slurry is poured; after the ardealite slurry is formed and reaches the strength and the water content required by the design, the calcium silicate board is mounted on the top surfaces of the C-shaped connecting pieces by using special screws for mounting the calcium silicate board. The composite floor gives play to the ardealite filling performance, and the buckling failure risk of the profiled steel sheet is reduced; the strength performance of the ardealite is exerted, and the bearing capacity and the deformation capacity of the floor are improved; the heat preservation, thermal insulation and fire resistance of the ardealite are exerted, and the thermal performance and fireproof ability of the floor are improved; and in addition, application of the ardealite in the floor can further open up a new direction for resourceutilization of the ardealite.

Description

technical field [0001] The invention belongs to the technical field of construction engineering, and in particular relates to a profiled steel plate-phosphogypsum-calcium silicate board composite floor and a manufacturing method thereof. Background technique [0002] Composite slabs are a form of slabs commonly used in steel structures. In the heavy steel structure, the composite floor is mainly composed of profiled steel plate and concrete. During construction, profiled steel plates are first laid on the steel beams, and the steel plates are fixed on the steel beams with cylindrical head welding nails, which are used as shear connectors for the composite floor slab. Subsequently, the reinforcement mesh sheet is laid and the concrete is poured. The biggest advantage of this composite floor is: 1. The profiled steel plate can be used as a formwork when pouring concrete, which reduces the workload of setting up supports and laying formwork during construction; 2. The profile...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): E04B5/40E04B5/32E04B1/76E04B1/94
CPCE04B1/76E04B1/942E04B1/945E04B5/32E04B5/40
Inventor 周理黄勇陈波包太
Owner GUIZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap