Aluminum alloy conductor flexible cable and preparation method thereof

A technology of aluminum alloy conductors and flexible cables, which is applied in the direction of metal/alloy conductors, cable/conductor manufacturing, conductors, etc., can solve the problems that flexible cables cannot use aluminum alloy as conductors, etc., and achieve uniform force balance and good corona resistance Flexible, easy-to-bend effect

Active Publication Date: 2021-01-22
TBEA DEYANG CABLE CO LTD
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem that aluminum alloy cannot be used as the conductor of the flexible cable in the prior art, the present invention provides a flexible cable and a method for preparing the cable. The conductor of the flexible cable of the present invention is an aluminum alloy material, and the aluminum alloy material Conductor elongation, tensile strength and electrical conductivity all meet the standards for flexible cable conductors, realizing that the conductors are replaced by aluminum alloys for copper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy conductor flexible cable and preparation method thereof
  • Aluminum alloy conductor flexible cable and preparation method thereof
  • Aluminum alloy conductor flexible cable and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] S1 material preparation: Weigh raw materials according to the ratio of Example 1 in Table 1: 0.1wt% magnesium ingot, 0.4wt% AlSi20 master alloy, 0.15wt% AlFe20 master alloy, 0.05wt% AlCu50 master alloy, 0.785wt% AlB3 master alloy, AlTi1 .2B0.5 master alloy 0.25wt%, AlRE10 aluminum rare earth master alloy 0.3wt%, the rest is aluminum ingots with a purity of 99.70%, and the raw materials are dried in a drying oven at a drying temperature of 110°C and a drying time of 6 hours;

[0035] Among them, the magnesium ingot was purchased from Shaanxi Tianyu Magnesium Industry Group Co., Ltd., the AlSi20 master alloy was purchased from Sichuan Lande High-Tech Industry Co., Ltd., the AlFe20 master alloy was purchased from Sichuan Lande High-Tech Industry Co., Ltd., and the AlCu50 master alloy was purchased from Sichuan Lande High-tech Industry Co., Ltd., AlB3 master alloy was purchased from Sichuan Lande High-Tech Industry Co., Ltd., AlTi1.2B0.5 master alloy was purchased from Sishu...

Embodiment 2

[0042] S1 material preparation: Weigh raw materials according to the ratio of Table 1 Example 2: 0.25wt% magnesium ingot, 0.6wt% AlSi20 master alloy, 1.25wt% AlFe20 master alloy, 0.1wt% AlCu50 master alloy, 1.05wt% AlB3 master alloy, AlB5Ti1 Master alloy 0.25wt%, AlRE10 aluminum rare earth master alloy 0.3wt%, the rest is aluminum ingots with a purity of 99.70%, and the raw materials are dried in a drying oven at a drying temperature of 140°C and a drying time of 5 hours;

[0043]Among them, the magnesium ingot was purchased from Shaanxi Tianyu Magnesium Industry Group Co., Ltd., the AlSi20 master alloy was purchased from Sichuan Lande High-Tech Industry Co., Ltd., the AlFe20 master alloy was purchased from Sichuan Lande High-Tech Industry Co., Ltd., and the AlCu50 master alloy was purchased from Sichuan Lande High-tech Industry Co., Ltd., AlB3 master alloy was purchased from Sichuan Lande High-Tech Industry Co., Ltd., AlB5Ti1 master alloy was purchased from Shandong Binzhou Hu...

Embodiment 3

[0049] S1 material preparation: weighing raw materials according to the ratio of Table 1 Example 3: 0.45 wt% magnesium ingot, 1.5wt% AlSi20 master alloy, 0.75wt% AlFe20 master alloy, 0.2wt% AlCu50 master alloy, 1.5wt% AlB3 master alloy, AlTi40 Master alloy 0.1wt%, AlRE10 aluminum rare earth master alloy 0.1wt%, the rest is aluminum ingots with a purity of 99.70%, and the raw materials are dried in a drying oven at a drying temperature of 80-150°C and a drying time of 5-10h;

[0050] Among them, the magnesium ingot was purchased from Shaanxi Tianyu Magnesium Industry Group Co., Ltd., the AlSi20 master alloy was purchased from Sichuan Lande High-Tech Industry Co., Ltd., the AlFe20 master alloy was purchased from Sichuan Lande High-Tech Industry Co., Ltd., and the AlCu50 master alloy was purchased from Sichuan Lande High-tech Industry Co., Ltd., AlB3 master alloy was purchased from Sichuan Lande High-tech Industry Co., Ltd., AlTi40 master alloy was purchased from Sichuan Lande Hig...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
angleaaaaaaaaaa
Login to View More

Abstract

The invention discloses an aluminum alloy conductor flexible cable and a preparation method thereof, and belongs to the field of flexible cables. The aluminum alloy conductor flexible cable comprisesone or more cabling sheath layers, a cabling and belting layer and conductor insulating wire cores from outside to inside in sequence, wherein the number of the conductor insulating wire cores is oneor more, cabling fillers are filled between the conductor insulating wire cores, and each conductor insulating wire core sequentially comprises a tensile strand, an aluminum alloy conductor and a wirecore insulating layer from inside to outside. The aluminum alloy conductor flexible cable not only has high conductivity, but further has excellent tensile strength and compressive creep resistance,the possibility of replacing copper with aluminum in the flexible cable is realized, the use cost of the flexible cable is reduced, and the wear resistance and the service life of the cable are improved due to light weight and excellent characteristics.

Description

technical field [0001] The invention relates to the field of flexible cables, in particular to a flexible cable with an aluminum alloy conductor and a method for preparing the cable. Background technique [0002] The cable industry usually uses copper as a conductor. Copper is the second largest strategic reserve material after oil. However, my country is seriously short of copper mine resources and is a country that uses copper. The safe and sustainable supply of copper raw materials has become a very important strategic issue. . [0003] Because the melting point of aluminum (660°C) is much lower than that of copper (1083.4°C), the industrial smelting of aluminum alloy materials greatly reduces the consumption of high energy-consuming resources such as coal and electricity, reduces greenhouse gas emissions, and promotes the harmonious development of social economy and ecological environment . Replacing copper with aluminum alloy has advantages in terms of technical indica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B7/02H01B7/04H01B7/17H01B7/18H01B7/22H01B7/28H01B7/29H01B1/02H01B13/00
CPCH01B1/023H01B7/02H01B7/04H01B7/17H01B7/18H01B7/1825H01B7/1865H01B7/1875H01B7/228H01B7/28H01B7/2806H01B7/2813H01B7/292H01B13/00Y02A30/14
Inventor 刘春昉周晶晶武志强杨鹤雷明宋明明吉鸿飞邓春艳王毅戚欢陈霞
Owner TBEA DEYANG CABLE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com