Preparation method of g-C3N4/Ti4O7 composite nano material and application of same in electrocatalytic oxygen reduction

A composite nanomaterial, g-c3n4 technology, applied in the field of nanomaterials, can solve the problems of high cathode overpotential, carbon carrier corrosion, poor stability, etc., achieve high oxygen reduction catalytic activity, improve oxygen reduction activity, and solve problems of poor stability Effect

Active Publication Date: 2021-02-05
XIDIAN UNIV
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high price of metal Pt and the reserves of only 66000t, it is an urgent problem to find an electrocatalyst that can replace metal Pt.
In addition, it has been reported that commercial Pt / C electrocatalysts have the following defects: (1) Pt nanoparticles will migrate and agglomerate on the carbon support; (2) Pt nanoparticles will dissolve and redeposit during the reaction process; (3) the cathode The air introduced into the air is generally not pure oxygen, but contains trace amounts of CO, H 2 Impurities such as S and hydrocarbons will be strongly adsorbed on the surface of the Pt / C electrocatalyst, preventing the oxygen reduction reaction and poisoning the Pt / C electrocatalyst; Shedding of nanoparticles (Carban, 2005, 43:1512-1516, J Catal, 1995, 154: 299-305, J PowerSources, 2006, 156: 128-141, Solid State Ionics, 2004, 175: 809-813)
In order to solve the problems of low reserves, high cost and poor stability of metal Pt existing in commercial Pt / C, it has been reported that titanium oxide TiO with better stability 2 、Ti 4 o 7 and Ti 3 o 5 Doped with noble metals Ir, Pd, Pt, etc. (Journal of Catalysis 358 (2018) 287–294, Applied Catalysis B: Environmental 201 (2017) 419–429), but the addition of noble metals makes the overpotential of the cathode in the oxygen reduction reaction relatively low. High, the increase in the load of the electrocatalyst leads to an increase in the reaction cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of g-C3N4/Ti4O7 composite nano material and application of same in electrocatalytic oxygen reduction
  • Preparation method of g-C3N4/Ti4O7 composite nano material and application of same in electrocatalytic oxygen reduction
  • Preparation method of g-C3N4/Ti4O7 composite nano material and application of same in electrocatalytic oxygen reduction

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 1. Preparation of g-C 3 N 4

[0033] Put urea into a 50.0mL corundum crucible, the amount of urea is half of the volume of the crucible, then wrap the corundum crucible with aluminum foil and put it in a muffle furnace, raise the temperature from room temperature to 550°C at a heating rate of 25°C / min, and keep it warm 4h, get g-C after natural cooling 3 N 4 .

[0034] 2. Preparation of g-C 3 N 4 / TiO 2 Complex

[0035] 0.1024g g-C 3 N 4 Ultrasonic dissolved in 40.0mL deionized water, stirred at 700rpm for 1h to obtain mixed solution A; at the same time, dissolved 7.5mL tetrabutyl titanate in 40.0mL ethylene glycol, stirred at 700rpm for 1h to obtain mixed solution B; then at 800rpm Under vigorous stirring, add the mixed solution B dropwise to the mixed solution A, and the dropwise addition is completed in 30 minutes to obtain the mixed solution C; finally, the stirred mixed solution C is hydrothermally reacted at 180°C for 10 hours, and after the reaction is ...

Embodiment 2

[0041] In step 2 of this example, 2 mL of tetrabutyl titanate was dissolved in 40.0 mL of ethylene glycol, and stirred at 700 rpm for 1 h to obtain mixed solution B; other steps were the same as in Example 1 to obtain g-C 3 N 4 / Ti 4 o 7 composite nanomaterials. The resulting g-C 3 N 4 / Ti 4 o 7 Ti in Composite Nanomaterials 4 o 7 The diameter of the nanoparticles is 20-30nm.

Embodiment 3

[0043] In the step 3 of the present embodiment, the addition amount of dopamine hydrochloride (PDA) is 0.10g, other steps are the same as embodiment 1, obtain g-C 3 N 4 / Ti 4 o 7 composite nanomaterials. The resulting g-C 3 N 4 / Ti 4 o 7 Ti in Composite Nanomaterials 4 o 7 The diameter of the nanoparticles is 15-30nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a g-C3N4 / Ti4O7 composite nano material and application of same in electrocatalytic oxygen reduction. The preparation method comprises the following steps: preparing g-C3N4 by using a high-temperature annealing method, preparing a g-C3N4 / TiO2 compound by using a hydrothermal reaction, and coating the surface of the g-C3N4 / TiO2 compound with a layer ofPDA to form a g-C3N4 / TiO2 / PDA composite precursor; and finally, annealing the g-C3N4 / TiO2 / PDA composite precursor at the temperature of 850-1000 DEG C in an inert environment to obtain the g-C3N4 / Ti4O7 composite nano material. The preparation method of the g-C3N4 / Ti4O7 composite nano material is simple, low in cost and environmentally friendly, and the particle size of Ti4O7 nano particles rangesfrom 10 nm to 30 nm. When the g-C3N4 / Ti4O7 composite nanomaterial is used as an oxygen reduction electrocatalyst, the g-C3N4 / Ti4O7 composite nanomaterial has high oxygen reduction activity, methanoltoxicity resistance and stability, and the problems of low commercial Pt / C reserves and high cost are solved.

Description

technical field [0001] The invention belongs to the technical field of nanometer materials, and in particular relates to a preparation method of an electrocatalyst, which is used for the oxygen reduction reaction of a cathode in a fuel cell. Background technique [0002] Energy issues have always plagued mankind, and people's demand for energy is increasing day by day. As a new technology with high efficiency and cleanliness, fuel cell has become the development hotspot in the field of new energy in the world today. Catalyst is a very important component in fuel cells, and its cost accounts for one-third of the cost of fuel cells. The most dominant reaction in the air cathode is the oxygen reduction reaction. The kinetics of the oxygen reduction reaction is very slow, and the main difficulty comes from the unusually strong O=O bond 498kJ / mol, which is difficult to break in the electrochemical state. Therefore, in order to accelerate the occurrence of oxygen reduction reac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01M4/86H01M4/88H01M4/90B82Y40/00
CPCH01M4/8878H01M4/8882H01M4/90H01M4/8647B82Y40/00H01M2004/8684Y02E60/50
Inventor 雷毅敏武德凯胡启航杨成哲
Owner XIDIAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com