Bio-based low-VOC water-based emulsion and preparation method thereof
A water-based emulsion and bio-based technology, applied in the field of polymer materials, can solve the problems of endangering human health, polluting air and the environment, and achieve the effects of increasing adhesion, reducing VOC emissions, and good light transmittance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0032] A bio-based low-VOC aqueous emulsion and a preparation method thereof, comprising the following steps;
[0033] Add 0.8g compound emulsifier (sodium dodecylbenzenesulfonate: alkylphenol polyoxyethylene ether ratio 1:3), 0.2g sodium hydrogen phosphate, 50g deionized water, 10g butyl acrylate, 10g isooctyl acrylate, then in N 2 Under the atmosphere, the temperature was set at 30°C, and the first mixture was obtained by emulsifying it at a speed of 500 r / min for 1 hour;
[0034] Adjust the stirring speed to 250r / min to stir the first mixture, heat up to 75°C, add 0.35g of initiator ammonium persulfate, will include 30g of diethyl fumarate, 10g of limonene oxide and the remaining 0.65g of initiator The mixture of the agent is added dropwise for 1h to obtain the second mixture:
[0035] Raise the temperature of the second mixture to 75°C for 6 hours, then cool down to 30°C, add 0.15g of triisopropanolamine, add a pH buffer to adjust the pH=8, stir with a stirrer for 20 min...
Embodiment 2
[0037] A bio-based low-VOC aqueous emulsion and a preparation method thereof, comprising the following steps;
[0038] Add 0.8g compound emulsifier (sodium dodecylbenzenesulfonate: alkylphenol polyoxyethylene ether ratio 1:3), 0.2g sodium hydrogen phosphate, 50g deionized water, 10g butyl acrylate, 20g isooctyl acrylate, then in N 2 Under the atmosphere, the temperature was set at 30°C, and the first mixture was obtained by emulsifying it at a speed of 500 r / min for 1 hour;
[0039] Adjust the stirring speed to 250r / min to stir the first mixture, heat up to 75°C, add 0.35g of initiator ammonium persulfate, will include 20g of diethyl fumarate, 10g of limonene oxide and the remaining 0.65g of initiator The mixture of the agent is added dropwise for 1h to obtain the second mixture:
[0040] The temperature of the obtained second mixture was raised to 75°C for 6 hours, then cooled to 30°C, 0.15g of triisopropanolamine was added, pH buffer was added to adjust the pH to 8, stirre...
Embodiment 3
[0042] A bio-based low-VOC aqueous emulsion and a preparation method thereof, comprising the following steps;
[0043] Add 0.8g compound emulsifier (sodium dodecylbenzenesulfonate: alkylphenol polyoxyethylene ether ratio 1:3), 0.2g sodium hydrogen phosphate, 50g deionized water, 10g butyl acrylate, 30g isooctyl acrylate, then in N 2 Under the atmosphere, the temperature was set at 30°C, and the first mixture was obtained by emulsifying it at a speed of 500 r / min for 1 hour;
[0044] Adjust the stirring speed to 250r / min to stir the first mixture, heat up to 75°C, add 0.35g of initiator ammonium persulfate, which will include 10g of diethyl fumarate, 10g of limonene oxide and the remaining 0.65g of initiator The mixture of the agent is added dropwise for 1h to obtain the second mixture:
[0045] The temperature of the obtained second mixture was raised to 75°C for 6 hours, then cooled to 30°C, 0.15g of triisopropanolamine was added, pH buffer was added to adjust the pH to 8, ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap