Formula and manufacturing method of slag ladle trunnion anti-sticking steel sheath

A steel sheath and trunnion technology, which is applied in the field of casting residual slag treatment, can solve the problems affecting the production rhythm, hidden dangers, and the inability of the slag tank spreader to be fully stuck, so as to reduce the hidden danger of slag tank reverse transportation and ensure smooth production. Effect

Inactive Publication Date: 2021-06-18
MAANSHAN IRON & STEEL CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a slag pot trunnion anti-stick steel sheath formula and its manufacturing method, which solves the problem of casting slag treatment. Turn the ladle directly into the slag pot. During the process of dumping the remaining steel slag, part of the steel slag will fall into the trunnion of the slag pot. Lifting, affecting the production rhythm, there are great safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Formula and manufacturing method of slag ladle trunnion anti-sticking steel sheath
  • Formula and manufacturing method of slag ladle trunnion anti-sticking steel sheath
  • Formula and manufacturing method of slag ladle trunnion anti-sticking steel sheath

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0020] see Figure 1-3 , the present invention provides a technical solution: a slag pot trunnion anti-stick steel sheath formula, the slag pot trunnion anti-stick steel sheath formula includes: slag 60-90%, lime 5-30%, bonding Agent 5-10%, the rest is refractory material, the refractory material is CaO and Al 2 o 3 The mixture is mixed according to the ratio of 3:1 to 6:1.

[0021] A method for manufacturing a slag tank trunnion anti-stick steel sheath, co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a formula and a manufacturing method of a slag ladle trunnion anti-sticking steel sheath, which relate to the technical field of casting residue treatment. According to the formula of the slag ladle trunnion anti-sticking steel sheath, the formula comprises 60-90% of slag, 5-30% of lime, 5-10% of a binder and the balance of a refractory material, and the refractory material is a mixture formed by mixing CaO and Al2O3 according to the proportion of 3: 1-6: 1. According to the formula and the manufacturing method of the slag ladle trunnion anti-sticking steel sheath, the matched trunnion sheath is manufactured, the sheath is placed at the position of the trunnion when the slag ladle receives slag steel, and the sheath is taken down when the slag ladle is hoisted. The formula effectively prevents slag steel from being adhered to the trunnion when the steel ladle is turned over casting residues, so that the lifting of the slag ladle is prevented from being influenced, the casting residue slag steel in the steel ladle is effectively prevented from being adhered to form a weight at the trunnion in the pouring process, so that the phenomenon that a slag ladle lifting appliance cannot be completely clamped into the trunnion for lifting the slag ladle is prevented, smooth production is ensured, and the hidden danger of pouring the slag ladle caused by the weight of the slag steel adhered to the trunnion of the ladle is reduced.

Description

technical field [0001] The invention relates to the technical field of casting slag treatment, in particular to a slag tank trunnion anti-sticking steel sheath formula and a manufacturing method thereof. Background technique [0002] Casting slag is the mixture of molten steel and slag left after the molten steel in the ladle is continuously cast or ingot cast. [0003] In terms of casting slag treatment, the treatment modes of all major steel mills are basically the same. They all use the crane to hang the ladle directly into the slag tank. The trunnion is bonded into a mound, so that the slag tank spreader cannot be completely stuck in for lifting the slag tank, which affects the production rhythm and poses a great safety hazard. Contents of the invention [0004] (1) Solved technical problems [0005] Aiming at the deficiencies of the prior art, the present invention provides a slag pot trunnion anti-stick steel sheath formula and its manufacturing method, which solve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66C04B35/622
CPCC04B35/66C04B35/62204C04B2235/3208C04B2235/3217
Inventor 张雷兰海峰邓勇张虎孔磊熊磊韩宝丁太强魏刚李应江李海波黄传根
Owner MAANSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products