High-toughness and high-cohesiveness C170-strength ultrahigh-strength fiber concrete and preparation method thereof

A technology of fiber concrete and high cohesion, which is applied in the field of building materials. It is a kind of mixed ramie fiber and basalt field. It can solve the problems of less active groups, affect the uniform dispersion of carbon nanotubes, and low relative solubility, and achieve increased Adhesiveness, cost reduction, and CO2 emission reduction effects

Active Publication Date: 2021-06-25
XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the surface of carbon nanotubes is complete and smooth, with few defects and active groups, and the relative solubility in water and various solutions or composite materials is low. There i...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-toughness and high-cohesiveness C170-strength ultrahigh-strength fiber concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0100] 1) Add 15 parts by mass of water reducer and 32 parts by mass of hydroxyl-modified single-walled carbon nanotube dispersion into two-thirds of the total water, and record it as mixed solution 1; Add 13.5 parts of shrinkage reducing agent and 2.8 parts of antifoaming agent into the water of one-third of the total water volume, and record it as mixed solution 2. After preparing 18 parts of carboxy-modified polyvinyl alcohol polymer, it is ready for use, and the total water volume is 100 Wherein, the carboxy-modified polyvinyl alcohol polymer is prepared from raw materials according to mass percentage: carboxy-modified polyvinyl alcohol 37%, water 62%, polyacrylate defoamer 1%;

[0101] 2) Divide 5.8 parts of ramie fiber, 975 parts of gravel, 720 parts of sand, 490 parts of cement, 75 parts of fly ash, 73 parts of straw ash, 55 parts of silica fume, 4.4 parts of nano silicon, and 10.6 parts of basalt fiber into Three parts, then spread a part of ramie fiber and basalt fibe...

Embodiment 2

[0110] 1) Add 16 parts by mass of water reducer and 30 parts by mass of hydroxyl-modified single-walled carbon nanotube dispersion to two-thirds of the total water, and record it as mixed solution 1; Add 14 parts of shrinkage reducing agent and 2.4 parts of defoamer to one-third of the total water volume, and record it as mixed solution 2. After preparing 20 parts of carboxy-modified polyvinyl alcohol polymers, the total water volume is 100 Wherein, carboxy-modified polyvinyl alcohol polymer is prepared from raw materials according to mass percentage: carboxy-modified polyvinyl alcohol 38.7%, water 60.3%, polyacrylate defoamer 1%;

[0111] 2) Divide 5.9 parts of ramie fiber, 975 parts of gravel, 715 parts of sand, 485 parts of cement, 73 parts of fly ash, 70 parts of straw ash, 57 parts of silica fume, 4.4 parts of nano silicon, and 10.5 parts of basalt fiber into Three parts, then spread a part of ramie fiber and basalt fiber evenly in the disc mixer, and then place a part of...

Embodiment 3

[0119] 1) Add 16.6 parts by mass of water reducer and 30 parts by mass of hydroxyl-modified single-walled carbon nanotube dispersion into two-thirds of the total water, which is recorded as mixed solution 1; 14 parts of shrinkage reducing agent and 2.6 parts of antifoaming agent are added to one-third of the total water, which is recorded as mixed solution 2. After the preparation of 19 parts of carboxyl-modified polyvinyl alcohol polymer is completed, the total water is 95 Wherein, carboxy-modified polyvinyl alcohol polymer is prepared from raw materials according to mass percentage: carboxy-modified polyvinyl alcohol 38.9%, water 60%, polyacrylate defoamer 1.1%;

[0120] 2) Divide 5.9 parts of ramie fiber, 975 parts of gravel, 722 parts of sand, 480 parts of cement, 72 parts of fly ash, 74 parts of straw ash, 60 parts of silica fume, 4.2 parts of nano silicon, and 10.5 parts of basalt fiber into Three parts, then spread a part of ramie fiber and basalt fiber evenly in the di...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Compressive strengthaaaaaaaaaa
Flexural strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses high-toughness and high-cohesiveness C170-strength ultrahigh-strength fiber concrete and a preparation method thereof. The concrete is prepared from cement, sand, gravel, fly ash, straw ash, silica fume, nano silicon, water, a water reducing agent, an exciting agent, a defoaming agent, a shrinkage reducing agent, ramie fibers, basalt fibers, hydroxyl modified single-walled carbon nanotube dispersion liquid and a carboxyl modified polyvinyl alcohol polymer according to the mixing ratio of (480-490): (715-725): 975: (70-75): (70-75): (55-60): (4.2-4.4): (95-100): (15-17): (13.5-14): (2.4-2.8): (13-14): (5.7-6): (10.4-10.7): (28-32): (18-20). The materials are evenly mixed at intervals through a layered stirring method, and discharging, forming and curing are conducted. The concrete mechanics including the structural steel bonding performance and the durability are remarkably improved, and the cooperative work capacity of the concrete and the structural steel is enhanced.

Description

technical field [0001] The invention belongs to the field of building materials, and is a compound mixed with ramie fiber, basalt fiber, carboxyl-modified polyvinyl alcohol polymer, hydroxyl-modified single-wall carbon nanotube dispersion liquid, straw ash, fly ash, silica fume and nano-silicon Concrete with high toughness, high cohesiveness, high durability and high volume stability, specifically relates to a high-toughness and high cohesion C170 strength ultra-high-strength fiber concrete and a preparation method thereof. Background technique [0002] In structural design, considering the requirements of use function, component stiffness and convenient construction, it is usually necessary to use different grades of concrete for different stress situations to meet the required compressive, flexural and splitting tensile strength of the component when it is loaded. And to ensure the bond strength of concrete and steel working together. Concrete materials with different gra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B111/34
CPCC04B28/04C04B2201/50C04B2111/343C04B2111/00017C04B2103/302C04B14/026C04B24/2623C04B18/248C04B14/02C04B14/06C04B18/08C04B18/101C04B18/146C04B14/04C04B14/46C04B22/124C04B22/143C04B24/122C04B2103/0068C04B2103/50Y02W30/91
Inventor 郑山锁段培亮阮升李亚辉郑跃董立国贺金川刘华张晓宇郑捷王斌董晋琦杨松张晓辉
Owner XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap