Single-component addition type thermocuring silicone rubber composition
A silicone rubber composition and an addition molding technology are applied in the field of one-component addition-type heat-curing silicone rubber compositions, which can solve the problem that the storage time and the heat-curing reaction time cannot be balanced, the storage period is short, and the colloid surface is prone to wrinkles and Air holes, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0102] Both ends is used as component A Viscosity 25 ℃ respectively with dimethyl vinyl-terminated 10000mPa · S is a dimethylpolysiloxane parts 60, specific surface area of 200m 2 / G, 40 parts of fumed silica, hexamethyl disilazane 8 parts, 2 parts of water, was added kneaded by a kneader, after uniformly mixed, further mixed at 150 deg.] C under vacuum for 1-3 hours, then added group a sub-component parts 40, 150 vacuum kneading deg.] C for 1 to 2 hours, cooled at room temperature to give a silicone rubber base.
[0103] To 100 parts of a silicone rubber base was added separately with both ends of component A Viscosity 25 ℃ dimethyl vinyl-terminated dimethyl polysiloxane 1000mPa · S 42 parts, both ends of the molecular chain with three vinyl-terminated molar fraction of 0.20% of 6 parts of methyl vinyl gum, having a Si-H group in the side chain methyl hydrogen polysiloxane (Si-H group content of 0.005mol / g) of component B 3.14 parts of component, 0.19 parts of ethynyl-9-fluo...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap