Glass strengthening liquid as well as preparation method and application thereof

A glass strengthening and glass technology, which is applied in the field of glass strengthening, can solve the problems of small increase in glass impact strength, adverse effects on the health of workers, and scratches, etc., to eliminate or passivate micro-cracks, reduce the proportion of scratches, and reduce effect of influence

Pending Publication Date: 2022-06-24
万津实业(赤壁)有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, hydrofluoric acid is toxic, and concentrated sulfuric acid is highly corrosive, which can adversely affect the health of workers
(2) Use alkaline agents (such as strong bases), basic additives (such as weak bases) and reinforcing agents (silicates) to chemically polish the glass. Compared with hydrofluoric acid polishing, this method is harmless to the environment , and basically has no effect on the human body, but if the content of alkaline reagents is low, the impact strength of the glass will be improved relatively little; The surface layer will cause a small amount or a large amount of silicon-oxygen bonds to break in the new surface layer, which may cause scratches. After the silicon-oxygen bonds are broken, the impact strength of the product will decrease, which is the opposite of the goal of improving the impact strength of the product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass strengthening liquid as well as preparation method and application thereof
  • Glass strengthening liquid as well as preparation method and application thereof
  • Glass strengthening liquid as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0072] The present invention also provides the above-mentioned preparation method of glass strengthening liquid, comprising the following steps:

[0073] The alkaline agent, surfactant, chelating agent, auxiliary agent and water are mixed.

[0074] In one embodiment, the preparation method of described glass strengthening liquid, comprises the steps:

[0075] According to the ratio, take 10% to 40% of the target water mass, add alkaline reagent first, stir to dissolve, cool down to 40 °C, add auxiliary, chelating agent, surfactant and the remaining amount of water in turn, stir evenly Afterwards, a glass strengthening liquid is obtained.

[0076] The present invention also provides the application of the glass strengthening liquid as described above. The technical solution is as follows:

[0077] A glass strengthening method, comprising the steps of:

[0078] Pretreating the glass, and then contacting the pretreated glass with the above-mentioned glass strengthening liquid...

Embodiment 1

[0087] This embodiment provides a glass strengthening liquid and a preparation method and application thereof.

[0088] (1) In terms of mass percentage, the composition of the glass strengthening liquid of the present embodiment is as follows:

[0089]

[0090] (2) the preparation method of the glass strengthening liquid of the present embodiment is as follows:

[0091] Take water that accounts for 20% of the target water mass, add sodium hydroxide first, stir to dissolve, cool down to 40 ° C, add glycerol, sodium gluconate, OEP-98, fast penetrant T and the remaining amount of water in turn, stir evenly to obtain Glass strengthening fluid.

[0092] (3) The steps of the strengthening method of the glass provided by the present embodiment are as follows:

[0093] The glass is subjected to cutting and CNC processing, polishing treatment and tempering treatment in sequence, and then the tempered glass is immersed in a glass strengthening solution with a temperature of 70 ° C ...

Embodiment 2

[0095] This embodiment provides a glass strengthening liquid and a preparation method and application thereof.

[0096] (1) In terms of mass percentage, the composition of the glass strengthening liquid of the present embodiment is as follows:

[0097]

[0098] (2) the preparation method of the glass strengthening liquid of the present embodiment is as follows:

[0099] Take water that accounts for 20% of the target water mass, add sodium hydroxide first, stir to dissolve, cool down to 40 ° C, add glycerol, sodium gluconate, OEP-98, fast penetrant T and the remaining amount of water in turn, stir evenly to obtain Glass strengthening fluid.

[0100] (3) The steps of the strengthening method of the glass provided by the present embodiment are as follows:

[0101] The glass is subjected to cutting and CNC processing, polishing treatment and tempering treatment in sequence, and then the tempered glass is immersed in a glass strengthening solution with a temperature of 70 ° C ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to glass strengthening liquid as well as a preparation method and application thereof. The glass strengthening liquid comprises the following components in percentage by mass: 0.8%-15% of an alkaline reagent, 0.05%-0.5% of a surfactant, 0.1%-1% of a chelating agent, 0.5%-5% of an auxiliary agent and 78.5%-98.55% of water, the auxiliary agent is selected from a borate compound and / or a polyol compound. The alkaline reagent can react with silicon dioxide in the glass to achieve the purpose of eliminating or passivating microcracks; the borate and / or polyhydric alcohol auxiliaries can reduce the damage rate of hydroxyl ions to a new surface layer, reduce the scratch ratio of the glass and improve the impact strength of the glass; the surfactant can increase the permeability and dispersity of the chemical polishing solution, so that the possibility of deposition of chemical polishing products on the glass surface is reduced; the chelating agent can avoid the influence of water quality on the strengthening result. In addition, hydrofluoric acid and concentrated sulfuric acid do not need to be used, harm to the human body and the environment is avoided, and operation is safe.

Description

technical field [0001] The invention relates to the technical field of glass strengthening, in particular to a glass strengthening liquid and a preparation method and application thereof. Background technique [0002] At present, electronic products such as tablet computers and mobile phones are pursuing lightness and thinness, and the glass cover plate is getting thinner and thinner. In order to reduce drop damage, the strength of the glass cover plate is required to be high enough. [0003] Glass is a typical brittle material, the main component is silicate double salt. There are many factors that affect the strength of glass, among which the existence of surface micro-cracks has the greatest impact on the actual strength of glass. Specifically, micro-cracks will occur in glass after cutting, CNC and polishing. In addition, the ion exchange in the chemical toughening process will also make the microcracks have a tendency to expand, resulting in a decrease in the impact s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C15/02
CPCC03C15/02
Inventor 彭晓林丁雄风王世军潘利军
Owner 万津实业(赤壁)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products