Method for synthesizing artificial bone from carboxylic apatite of coral

A technology of coral hydroxyapatite and hydroxyapatite, which is applied in the field of artificial bone, can solve the problems that there are no public reports on the preparation process, and achieve the effect of good bone defect fusion, good effect and high compressive strength

Inactive Publication Date: 2006-01-11
SUN YAT SEN UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] There have been some reports in the literature on the use of natural mineral material coral as raw material to modify and synthesize hydroxyapatite (CHA) artificial bone, but there is no public report on its specific preparation process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] 1. Take 50g (block) of natural mineral material coral and cut it into three pieces of 1×1×1cm, 2.8×1.2×1.5cm, 6.3×1.5×0.65cm on a diamond cutter, weighing 19.0g.

[0048] 2. Place the three cut raw material samples in a beaker filled with deionized distilled water, and clean them in an ultrasonic cleaner.

[0049] 3. Design the synthetic experimental conditions, the pressure is 100×10 5 Pa, the temperature is 220°C, and the synthesis is carried out in an autoclave. Calculate according to the volume of the raw material sample, and the filling degree of the added medium liquid is 0.75, and calculate the amount of the medium solution to be added according to the filling degree.

[0050] 4. The medium is a saturated aqueous solution of diammonium hydrogen phosphate, the concentration is 3M, and the pH of the solution is 8.5 when measured with a pH meter.

[0051] 5. Put the raw material samples and the medium solution into the autoclave together, and place the sealing plug...

Embodiment 2～6

[0066] Synthetic process with reference to Example 1. The process condition parameters used in each embodiment, the chemical composition and pore parameters of the obtained CHA artificial bone products are shown in Table 2 to Table 4 respectively.

[0067] Example

[0068] Example

[0069] The electron microscope energy spectrum component analysis results of Table 3 show that the CaO and P of the CHA artificial bone synthesized by the method of the present invention under different temperature and pressure conditions 2 o 5 The content is similar to that of human bone, so it has good compatibility.

[0070] Example

[0071] The result of table 4 shows that the pore parameters of the CHA artificial bone synthesized by the inventive method under different temperature and pressure conditions are similar to those of human bone, indicating that the CHA synthetic artificial bone prepared by the inventive method has good transmission properties to liquid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

An artificial coral hydroxy apatitis (CHA) bone for medical purpose is prepared from coral through hydrothermal reaction in the diammonium hydrogen phosphate plus hydrothermal liquid system under high-temp and high-pressure condition to convert the CaCO3 of coral to Ca5(PO4)3(OH) which is just the artificial bone. Its advantages are high compression strength, high porosity (24.86-65.71%), no toxic by-effect and good biologic compatibility.

Description

technical field [0001] The invention relates to an artificial bone for orthopedic medical treatment, in particular to a method for synthesizing a coral hydroxyapatite (CHA) artificial bone. Background technique [0002] Bone defect is a common problem in orthopedics. Bone fusion is a commonly used method in orthopedics. Every year in my country, thousands of people are amputated or resected to disability due to comminuted fractures or osteonecrosis caused by various industrial injuries, car accidents, and accidents. Synthetic Artificial bone grafts can repair damaged limbs of patients, free them from disability and relieve their pain. The preparation of an ideal synthetic artificial bone is a major problem that the orthopedic medical community is eager to solve. [0003] The hotspots and main contents of bone tissue engineering research focus on several aspects: seed cells, scaffold materials, and bioactive factors. Among them, the scaffold material is a very important part...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/12C01B25/32
Inventor 李兆麟李文薄遵昭尹庆水张余
Owner SUN YAT SEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com