Cordierite nucleated glass prepared by using flyash and its preparation method

A technology of glass-ceramics and fly ash, applied in the field of ceramic materials

Inactive Publication Date: 2003-12-10
CHINA UNIV OF GEOSCIENCES (WUHAN)
View PDF0 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no report on the cordierite glass-ceramic prepared by using fly ash and the preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A cordierite glass-ceramic prepared from fly ash. When it is used to prepare kiln furniture, its formula is 61-66wt% of fly ash, 6-11wt% of aluminum oxide powder, 20-25wt% of basic magnesium carbonate (also known as magnesium carbonate) powder, methyl cellulose 3 -5wt%, water 3-6wt%. If it is used to prepare honeycomb products, its formula is 48-52wt% of fly ash, 5-9wt% of aluminum oxide powder, 15-20wt% of basic magnesium carbonate powder, 5-9wt% of methylcellulose, sodium stearate 1wt%, water 18-25wt%.

[0021] Preparation:

[0022] 1. Prepare kiln furniture. 1), ingredients: 61-66wt%, aluminum oxide powder 6-11wt%, basic magnesium carbonate (also known as magnesium carbonate) powder 20-25wt%, methylcellulose 3-5wt%, water 3-6wt%. ; Fully and evenly mix the above ingredients;

[0023] 2), manufacturing the green body: press molding with a press to make the green body;

[0024] 3), dry green body;

[0025] 4) High-temperature crystallization: the dried green bod...

Embodiment 2

[0030] Example 2: A cordierite glass-ceramic prepared with fly ash. When it is used to prepare kiln furniture, its formula is fly ash 59-64wt%, alumina powder 8-12wt%, magnesite (MgCO 3 ) powder 20-24wt%, methylcellulose 3wt%, water 5wt%. If it is used to prepare honeycomb products, its formula is 45-49wt% of fly ash, 6-10wt% of alumina powder, magnesite (MgCO 3 ) powder 15-19wt%, methylcellulose 4-8wt%, sodium stearate 1wt%, water 20-25wt%.

[0031] Its preparation method is basically the same as Example 1.

Embodiment 3

[0032] Example 3: A cordierite glass-ceramic prepared with fly ash. When it is used to prepare kiln furniture, its formula is 62-67wt% of fly ash, 9-13wt% of aluminum oxide powder, 15-19wt% of feldspar powder, 3wt% of methylcellulose, and 5wt% of water. If it is used to prepare honeycomb products, its formula is 50-55wt% of fly ash, 6-10wt% of aluminum oxide powder, 14-19wt% of magnesium hydroxide powder, 4-8wt% of methylcellulose, sodium stearate 1wt%, water 20-25wt%.

[0033] Its preparation method is basically the same as Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to view more

Abstract

The present invention relates to an iolite pyroceram prepared by using flyash as main raw material and its preparation method. Its composition includes (wt%) 45-77% of flyash, 5-15% of alumina powder of bauxite, 10-25% of basic magnesium carbonate or magnesite or brucite or magnesium oxide powder, 3-10% of methyl cellulose and 3-30% of water.

Description

technical field [0001] The invention belongs to the field of ceramic materials, and in particular relates to a glass-ceramic prepared from fly ash and a preparation method thereof. Background technique [0002] The phase composition in general fly ash is mainly glass microspheres, quartz and mullite, wherein the content of glass microspheres is greater than 60wt%; the content of glass phase in fly ash less than 300 mesh accounts for 90wt% of this part of fly ash %. The crystalline bulk material transformed from glass is called glass-ceramic. At present, there is no report on cordierite glass-ceramics prepared with fly ash and its preparation method. Contents of the invention [0003] The object of the present invention is to provide a kind of cordierite glass-ceramic prepared with fly ash and preparation method, and this material has very low coefficient of linear thermal expansion [1.46.10 -6 / °C (20-1000°C)], suitable for high-temperature engineering materials, such a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C10/00
CPCC03C10/0063
Inventor 何涌
Owner CHINA UNIV OF GEOSCIENCES (WUHAN)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap