High water absorbing and retaining composite containing illite clay mineral and method for preparing the same

A kind of clay mineral, composite material technology

Inactive Publication Date: 2004-11-03
CHINA UNIV OF GEOSCIENCES (WUHAN)
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among the above series of varieties, some raw material costs are relatively high, some have low absorption rate of calcium and magnesium ion aqueous solutions, some have poor salt tolerance, and some have complicated processes and high equipment requirements.
The water-absorbing and water-retaining materials used for agricultural and forestry purposes are limited due to the high cost of raw materials, low absorption rate of calcium and magnesium ion aqueous solution, and poor salt resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] In 300 grams of acrylic acid solution with a concentration of 15% and a neutralization degree of 100%, add 0.0031 grams of N, N'-methylenebisacrylamide and 0.0212 grams of potassium persulfate under stirring, dissolve, and then grind the superfine 10 grams of illite clay mineral (content greater than 50%) was added thereto, and ultrasonically dispersed for 10 minutes. After the mixed material was heated in the reactor at 50°C for 7 hours, the temperature was raised to 30°C for 1 hour, and the resulting gel was dried at 150°C for 1 hour, and then crushed mechanically to obtain the final product.

Embodiment 2

[0033] In 300 grams of acrylic acid solution with a concentration of 30% and a neutralization degree of 80%, add 0.022 grams of N, N'-methylenebisacrylamide and 0.425 grams of potassium persulfate under stirring, dissolve, and then grind the ultrafine 50 grams of illite clay mineral (content greater than 90%) was added therein, and ultrasonically dispersed for 20 minutes. The mixed material was heated at 70°C in the reactor for 3 hours, then raised to 10°C for 2 hours, and the resulting gel was dried at 50°C under vacuum for 5 hours, and then crushed mechanically to obtain the final product.

Embodiment 3

[0035] In 200 grams of acrylic acid solution with a concentration of 45% and a neutralization degree of 20%, add 0.005 grams of N, N'-methylenebisacrylamide and 0.050 grams of potassium persulfate under stirring, dissolve, and then grind the ultrafine 30 grams of illite clay mineral (content greater than 60%) is added therein, and the colloid mill is dispersed. After the mixed material was heated at 60°C for 4 hours in the reactor, the temperature was raised to 20°C for 3 hours, and the resulting gel was dried at 110°C for 5 hours, and then crushed mechanically to obtain the final product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The water absorbing and maintaining composite material consists of water soluble unsaturated ethylene monomer, illite-clay mineral in the amount of 2-300 wt% of the ethylene monomer, and water soluble free radical polymerization initiator in the amount of 0.001-1 wt% of the ethylene monomer. The preparation process includes adding illite-clay mineral into 5-50 % concentration water soluble unsaturated ethylene monomer solution with water soluble free radical polymerization initiator or water soluble free radical polymerization initiator and crosslinking agent, dispersing, heating to 20-90 deg,c for polymerization of 1-10 hr, drying of the polymerized product at 40-150 deg.c and crushing mechanically to obtain grain product. The water absorbing and maintaining composite material has low cost, high absorption to calcium and magnesium ion aqua and high salt tolerance, and is suitable for use in agriculture and forestry.

Description

technical field [0001] The invention relates to a superabsorbent and water-retaining agent and a preparation method thereof, in particular to a superabsorbent and water-retaining material used in agriculture and forestry and a preparation method thereof. Background technique [0002] In recent years, superabsorbent and water-retaining agents have been widely used as sanitary products and industrial materials. Among the known superabsorbent and water-retaining agents, there are several series of varieties: vinyl water-soluble monomer homopolymers, copolymers, starch-grafted vinyl water-soluble monomer series, cellulose-grafted vinyl water-soluble Sexual monomer series, cross-linked carboxymethyl cellulose, etc. In the composite series, there are composites of superabsorbent resins and inorganic gels, and composites of superabsorbent resins and organic substances. Among the above series of varieties, some raw material costs are relatively high, some have low absorption rate ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F2/44C08K3/34C08L33/00
Inventor 范力仁沈上越王春龙
Owner CHINA UNIV OF GEOSCIENCES (WUHAN)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap