Thermoplastic elastomers exhibiting superior barrier properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
examples
[0034]Table 2 shows two examples of the present invention, in comparison with a control (Comparative Example A) and four comparison examples (Comparative Examples B-E) representing a TPE-S with either amorphous or crystalline nylon which does not contain organoclay.
[0035]All formulations of Examples 1-2 and Comparative Examples A-E had the same SIBS TPE-S matrix. All formulations of Examples 1-2 and Comparative Examples B-E had the same SIBS TPE-S matrix and antioxidant. Comparative Examples B and D offered a direct comparison with Example 1, while Comparative Examples C and E offered a direct comparison with Example 2. Only the type of polyamide was different.
[0036]All of Examples 1-2 and B-E were made using a twin-screw extruder set at 238° C. in all zones, rotating at 500 rpm. All ingredients were added before Zone 1. The melt-mixed compound was pelletized for further handling.
[0037]Pellets of all Examples 1-2 and A-E were molded into tensile test bars using a Demag injection mol...
PUM
Property | Measurement | Unit |
---|---|---|
Percent by mass | aaaaa | aaaaa |
Percent by mass | aaaaa | aaaaa |
Percent by mass | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap