Multifunctional ablation-resistant adhesive for thermal protection and method for preparing same

A heat protection and ablation-resistant technology, applied in the direction of adhesives, etc., can solve problems such as complex construction technology, and achieve the effects of low line ablation rate, good adhesion, and good mechanical properties

Inactive Publication Date: 2009-02-11
SHANDONG UNIV
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the specific construction, the ablation-resistant material and the adhesive are two kinds of materials, and the construction process is relatively complicated.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional ablation-resistant adhesive for thermal protection and method for preparing same
  • Multifunctional ablation-resistant adhesive for thermal protection and method for preparing same
  • Multifunctional ablation-resistant adhesive for thermal protection and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] The raw material components of the ablation-resistant adhesive for multifunctional thermal protection of the present invention are as follows, all in parts by weight:

[0057] Polysiloxane I 50

[0058] Polysiloxane II 50

[0059] 105 resin 5

[0060] Silica 15

[0061] Toner 8

[0062] Chromium trioxide 3

[0063] Zinc oxide 3

[0064] γ-Glycidoxypropyltrimethoxysilane 1

[0065] Hexamethyldisilazane 1.5

[0066] Orthoethyl silicate 2

[0067] Stannous octoate 1.4

[0068] Refer to the literature (Feng Shengyu, Zhang Jie, Li Meijiang, Zhu Qing addendum, organosilicon polymer and its application, Chemical Industry Press, 2004, Chapter 3) to introduce the method to prepare polysiloxane I or II. For example: Add octamethylcyclotetrasiloxane, various modified cyclosiloxanes, catalysts, etc. in proportion 2 In the reaction flask of conduit and reflux device, under N 2 Under protection, slowly heat to 80-90° C., stir and keep warm for 1-2 hours, then add end-cappi...

Embodiment 2

[0075] The raw material components are as follows, all in parts by weight:

[0076] Polysiloxane I 40

[0077] Polysiloxane II 60

[0078] 105 resin 4.5

[0079] Silica 20

[0080] Toner 8

[0081] Chromium trioxide 3

[0082] Zinc oxide 3

[0083] γ-Glycidoxypropyltrimethoxysilane 1

[0084] Hexamethyldisilazane 1.5

[0085] Orthoethyl silicate 2

[0086] Stannous octoate 1.4

[0087] Referring to the preparation method of Example 1, the ablation-resistant adhesive for multifunctional thermal protection was obtained. Its properties are: ablation rate 0.170mm / s; tensile strength 3.59MPa; density 1.19g / cm 3 ; Bonding and peeling strength of steel is 3.46MPa.

Embodiment 3

[0089] The raw material components are as follows, all in parts by weight:

[0090] Polysiloxane I 45

[0091] Polysiloxane II 55

[0092] 105 resin 4.3

[0093] Silica 18

[0094] Toner 10

[0095] Chromium trioxide 3

[0096] Zinc oxide 3

[0097] γ-Glycidoxypropyltrimethoxysilane 1

[0098] Hexamethyldisilazane 1.5

[0099] Orthoethyl silicate 2

[0100] Stannous octoate 1.4

[0101] Referring to the preparation method of Example 1, the ablation-resistant adhesive for multifunctional thermal protection was obtained. Its properties are: ablation rate 0.176mm / s; tensile strength 3.45MPa; density 1.18g / cm 3 ; Bonding and peeling strength of steel is 3.25MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
ablation rateaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The present invention discloses one kind multifunctional protecting ablation resisting adhesive. The adhesive consists of polysiloxane 50-130 (in weight portions, the same below), polysiloxane-II 50-70, epoxy resin 0-10, No. 105 resin 0-5, white carbon black 10-20, carbon powder 5-15, chromium oxide 2-8, zinc oxide 3-10, adhesion promoter 1-3, stabilizer 0-5, crosslinking agent 2-5, and catalyst 0.5-3. The adhesive of the present invention has small density, low ablation rate, excellent adhesion to several kinds of matrix, simple preparation process, low cost and other advantages.

Description

technical field [0001] The invention relates to an adhesive and a preparation method thereof, in particular to an ablation-resistant adhesive for multifunctional heat protection and a preparation method thereof, belonging to the technical field of special advanced materials for heat protection. Background technique [0002] With the rapid development and progress of science and technology, higher and more stringent requirements are constantly put forward for thermal protection materials. Ablation-resistant materials can effectively protect various substrates from erosion under harsh conditions such as high temperature, high pressure, and high-speed scour airflow, and thus are increasingly widely used. [0003] Ablation-resistant materials should have the following properties: (1) large specific heat - can absorb a large amount of heat; (2) small thermal conductivity - difficult to transfer heat to the inside; (3) high melting point; (4) has Viscous, forms a carbonized layer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J183/04
Inventor 冯圣玉陈剑华张圣有李子龙颜梅江金强施伟李美江朱庆增张洁于淑歧
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com