Thermoplastic resin composition and molded product
一种热塑性树脂、组合物的技术,应用在热塑性树脂组合物及成型物领域,能够解决没有涉及聚碳酸酯/聚乳酸组合物耐水解性等问题
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1~7 and comparative example 1~3
[0123] The components (A) to (C) were mixed according to the ratio shown in Table 1, and supplied to a bent type (benttype) two-axis extrusion molding machine (model name TEM35, manufactured by Toshiba Machine Co., Ltd.), at 240°C Melt kneading to make granules. In addition, in all Examples and Comparative Examples, 0.1 parts by mass of a phosphorus-based antioxidant (manufactured by Asahi Denka Industry Co., Ltd., trade name "Adecastab PEP-36") and a phenolic antioxidant Irganox 1076 (Chiba. Specialty Chemicals, trade name) was used as a stabilizer.
[0124] The obtained pellets were dried at 100° C. for 10 hours, and then injection molded at a molding temperature of 240° C. (mold temperature 40° C.) to obtain test pieces using the resins of the corresponding examples and comparative examples. Using the obtained test piece, the performance was evaluated respectively according to the above-mentioned performance evaluation method.
[0125] Table 1
[0126] Example...
PUM
Property | Measurement | Unit |
---|---|---|
glass transition temperature | aaaaa | aaaaa |
viscosity average molecular weight | aaaaa | aaaaa |
degree of polymerization | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap