Nickel zinc ferrite low temperature high density production method and its product

A technology of nickel-zinc ferrite and manufacturing method, which is applied in the direction of magnetism of inorganic materials, can solve the problems of lowering the Curie temperature and deterioration of characteristics, and achieve the effects of high Curie temperature, high magnetic permeability, and high saturation magnetic induction intensity

Inactive Publication Date: 2008-01-16
TDG HLDG CO LTD
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although high sintering temperature can achieve high sintering density and high magnetic permeability, it will deteriorate other characteristics, such as key indicators such as saturation magnetic induction
At the same time, in order to obtain high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nickel zinc ferrite low temperature high density production method and its product
  • Nickel zinc ferrite low temperature high density production method and its product
  • Nickel zinc ferrite low temperature high density production method and its product

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0023] 47.5~49.5mol% Fe 2 O 3 , 3.6~6.5mol% of CuO, 30~35mol% of ZnO, the rest is the main component of NiO, pre-fired after mixing, add 0.01~0.4wt% of Ti 2 O 5 , 0.01~0.5wt% Bi 2 O 3 , 0.01~0.5wt% of V 2 O 5 , 0.01~0.5wt% MoO 3 , 0.01~0.5wt% Cr 2 O 3 , 0.01~0.5wt% Nb 2 O 5 At least one of the secondary components, namely impurities, is then pulverized, and a small amount of binder PVA is added to make a slurry with a certain viscosity, which is granulated by spraying to make particles with 80-220 mesh. Then, the particles are pressed into the required After a sintering process with a sintering temperature of about 200℃ lower than that of the prior art, the blank can be highly densified (5.2g / cm 3 Above).

[0024] The main components and auxiliary components shown in Table 1 are the embodiments of the present invention (A, B, C, F, G, I, J). After testing, the density is 5.2g / cm 3 The sintering temperature required for the finished product and the permeability, saturation magnetic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method to produce nickel zinc ferrite with lower temperature and high intensity and nickel zinc ferrite with high magnetic permeability produced with the method. The main components of raw materials adopted in the method are converted into 47.5-49.5mol percent Fe2O3, 3.6-6.5mol percent CuO and 30-35mol percent ZnO, and the rest is NiO. Apart from the main components, the others are converted into one of the minor components, including.01-0.4wt percent Ti2O5, 0.01-0.5wt percent Bi2O3, 0.01-0.5wt percent V2O5, 0.01-0.5wt percent MoO3, 0.01-0.5wt percent Cr2O3, and 0.01-0.5wt percent Nb2O5. The finished product is obtained through steps of material batching, mixing, pre-heating, crushing, grain-making, molding, and sintering. Minor components are mixed after the main components are preheated. The method can realize as high intensity as 5.2g/cm3 and above to enhance the magnetic permeability at a sintering temperature of 200 DEG C lower than the current technique. The method can also increase magnetic inversion temperature and saturation magnetic sensing intensity.

Description

technical field [0001] The invention relates to a high-permeability nickel-zinc (NiZn) ferrite and a manufacturing method thereof, in particular to a manufacturing method and a ferrite material of the high-permeability nickel-zinc ferrite that can be sintered at low temperature. Background technique [0002] High permeability NiZn ferrite core can effectively absorb electromagnetic interference signals to achieve the purpose of anti-electromagnetic interference. With the development of electronic products to high frequency, high speed, and high assembly density, anti-EMI cores must be used in various electronic and power circuits. High permeability NiZn ferrite cores have dual advantages, which can greatly reduce the size of the device volume, and can increase the operating frequency. [0003] The sintering temperature of high permeability NiZn ferrite is generally 1050-1200°C. Under the same formulation conditions, the magnetic core sintered body must have a high sintered ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01F1/10
Inventor 吴利强吴冬华许晓亮
Owner TDG HLDG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap