Developer roll and method of producing the same

A technology for developing rollers and metal shafts, which is applied to equipment, coatings, instruments, etc. in the electrical recording process using charge patterns, which can solve problems such as insufficient electrical conductivity, reduced surface roughness of developing rollers, oozing pollution, etc., and achieve product Uniform resistivity, less contamination of the photosensitive drum, and high production efficiency

Inactive Publication Date: 2008-05-14
ZHEJIANG DONGYANG CHENGJI ELECTRO MECHANICS CO LTD
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The developing roller of the present invention adopts two kinds of liquid prepolymers to make polyurethane elastomers, wherein the prepolymer-R liquid includes a conductive substance whose weight percentage is 2-8%, and the prepolymer-P liquid includes its weight percentage It is 50-70% isocyanate, which solves the problem of insufficient conductivity and oozing pollution of the developing roller at low temperature; in addition, a developing surface layer with a thickness of 10-40 μm is sprayed on the surface of the polyurethane elastomer, so that the development Reduced surface roughness of the roll and uniform composition distribution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Developer roll and method of producing the same
  • Developer roll and method of producing the same
  • Developer roll and method of producing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0049] Dispersant described in embodiment 2 is by weight percentage and is acrylic acid copolymer: 35%; Propylene glycol methyl ether acetate: 40%; Ethylene glycol butyl ether: 25% make; Described mixed resin is made of Acrylic resin by weight percentage: 65%; Isobutyl alcohol: 8%; Methyl isobutyl ketone: 7%; the rest is made of xylene; the defoamer is polymerized by weight percentage Ethyl glycolate: 8%; Ethyl glycol butyl ether: 1.5%; the rest is made of solvent gasoline; the organic solvent is acetone;

Embodiment 3

[0050] Dispersant described in embodiment 3 is by weight percent acrylic acid copolymer: 40%; Propylene glycol methyl ether acetate: 25%; Ethylene glycol butyl ether: 35% make; Described mixed resin is made of Acrylic resin by weight percentage: 70%; Isobutyl alcohol: 7%; Methyl isobutyl ketone: 8%; the rest is made of heavy aromatics; the defoamer is polymerized by weight percentage Ethyl glycolate: 7%; Ethyl glycol butyl ether: 1%; the rest is made of solvent gasoline; the organic solvent is butanone;

Embodiment 4

[0051] Dispersant described in embodiment 4 is by weight percent acrylic acid copolymer: 45%; Propylene glycol methyl ether acetate: 30%; Ethylene glycol butyl ether: 25% make; Described mixed resin is made of Acrylic resin by weight percentage: 75%; Isobutyl alcohol: 10%; Methyl isobutyl ketone: 5%; The rest is the mixing of toluene and xylene; Silicone resin polymer: 25%; ethyl glycolate: 6%; butyl glycol ether: 1%; the rest is made of solvent gasoline; the organic solvent is acetone;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to view more

Abstract

The invention relate to a developing roller and a preparation method thereof. The developing roller comprises a metallic axle. The metallic axle is adhered with a polyurethane elastomer. The surface of the polyurethane elastomer is coated with a developing surface layer the thickness of which is 10 to 40Mum. The polyurethane elastomer is made of prepolymer-R solution or prepolymer-P solution. The prepolymer-R solution comprises conductive substances the weight percentage of which is 2 to 8 percent. The prepolymer-P solution comprises TDI the weight percentage of which is 50 to 70 percent. The developing roller is made of prepolymer materials. Therefore, the invention has the advantages of proper elasticity, good wear resistance, good heat resistance, good chemical stability, and low compression deformation rate and is not likely to pollute the OPC drum.

Description

technical field [0001] The invention relates to a developing roller and a preparation method thereof. The developing roller is used in non-magnetic developing devices, such as printers, duplicators, facsimile machines and the like. Background technique [0002] Copiers, printers, and facsimile machines charge and expose the photosensitive drum through the charging roller to form an electrostatic latent image, and then transfer the toner to the electrostatic latent image part on the photosensitive drum through the developing roller, and the toner image is transferred to the paper to be heated and shaped to form Finally print the text image. [0003] There are charging rollers and developing rollers in the toner cartridges of copiers, printers, and fax machines. The charging rollers and developing rollers in the prior art use conductive rubber to make conductive elastomers, and then a metal shaft is fixed in the rubber elastic body. Synthetic rubber It is also difficult to ke...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G03G15/08F16C13/00C08J7/04C08L75/04
Inventor 陆柏松
Owner ZHEJIANG DONGYANG CHENGJI ELECTRO MECHANICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap