Calcium monofluorophosphate rust-proofing powder

A technology of calcium fluorophosphate and anti-rust powder, which is applied in the direction of anti-corrosion coatings, chemical instruments and methods, and compositions for inhibiting chemical changes, etc., can solve the problems of unstable anti-rust performance, achieve extended storage period, convenient use, The effect of excellent performance

Inactive Publication Date: 2008-05-21
武汉市大汉科技发展有限公司
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The composite iron-titanium powder that has appeared in recent years has some impuriti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0014] Example 1

[0015] Take 97.7kg of processed natural phosphate and fluorite mixture with a fineness of 500 mesh, add 1.8kg of intercalated nano rectorite powder and 0.5kg of titanium-based nano powder, mix and stir evenly to obtain fluorophosphoric acid Calcium antirust powder 100kg.

Example Embodiment

[0016] Example 2

[0017] Take 8kg of processed natural phosphate and fluorite mixture with a fineness of 600 mesh, add 8kg of intercalated nano rectorite powder and 3kg of titanium-based nano powder, mix and stir evenly to obtain calcium fluorophosphate antirust Powder 100kg.

Example Embodiment

[0018] Example 3

[0019] Take the processed natural phosphate and fluorite mixture 94.5 with a fineness of 1000 mesh into the intercalated nano-retorite powder 4kg and titanium-based nano-powder 1.5, mix and stir evenly to obtain calcium fluorophosphate anti-rust powder 100kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides rust-proof powder of calcium fluophosphate; the components have follwing weight percentages: the remainder of natural phosphate and fluorite, 2 weight percent to 8 weight percent of processed rectorite powder, and 0.5 weight percent to 3 weight percent of group nano material. The rust-proof powder has the advantages of the strongest anti-rust performance and the most stable performance; the rust-proof powder is the best anti-rust paint in the world. The invention has broad adaptability and can be used for various kinds of oily paint; the prepared aqueous paint can be stored for a long time with no stratification or corrosion; no additional corrosion inhibitor or anti-settling agent is needed; the invention not only suits the steel surface, but also suits the anti-rust paint for copper, aluminum and other metal surfaces.

Description

technical field [0001] The invention relates to the technical field of antirust pigments, in particular to calcium fluorophosphate antirust powder for improving the antirust ability of antirust paints. Background technique [0002] Anti-rust paint is a necessary anti-rust material for steel components, and there must be anti-rust ingredients in the anti-rust paint, that is, anti-rust pigments. Traditional antirust pigments include red lead powder, iron red powder, aluminum tripolyphosphate powder, zinc silicate, and chromate. Some of the above antirust pigments contain heavy metals, and some do not contain heavy metals. The composite iron-titanium powder that has appeared in recent years has some impurities in its carrier component (phosphate), which makes its antirust performance unstable. Therefore the domestic market is in urgent need of a novel antirust pigment with excellent antirust performance, stable quality, non-toxic and harmless, easy to use, and adaptable to oil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09K15/02C09D5/08
Inventor 金广泉
Owner 武汉市大汉科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com