Modified red stilbite rubber reinforced additive and preparation method thereof
A technology of hematilite and additives, which is applied in the direction of chemical instruments and methods, inorganic pigment treatment, fibrous fillers, etc., which can solve the problems of difficult filling, insufficient surface adsorption capacity, insufficient improvement of rubber processing performance and physical properties, etc. problems, to achieve specific surface area and compatibility improvement, strong competitiveness and promotion and application value, and improve the effect of various performance indicators
Inactive Publication Date: 2008-08-13
GUANGXI NORMAL UNIV
View PDF0 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The hematilite used in this application has only been pulverized without modification, and its surface adsorption capacity is not strong enough to be easily filled into the network structure of vulcanized rubbe
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0011] Using the hematilite ore produced in Ziyuan County, Guangxi as the main raw material, the raw ore was washed, crushed and processed to 60-80 mesh, and 60g of hematite was modified by soaking in 120ml of 5% hydrochloric acid solution for 40 minutes. After modification Neutralize with 5g of calcium oxide, filter and wash until the pH value of the solution is 6.5, and dry the powder until the water content is less than 1%, to obtain the modified hematilite.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more
Abstract
The invention relates to a modified epidesmine rubber reinforcement additive and preparation method thereof, which is made from epidesmine raw ore processed by washing, crashing, hydrochloride immersion, calcium oxide neutralization, washing, drying and packing. The advantages of the invention are specific surface and compatibility of the epidesmine are improved after being modified, surface adsorbing power are enhanced, the epidesmin is easy to fill in the rubber mesh organization, the rubber is easier to get into the bee-like structure, and the processing performance and physical property of the rubber can be enhanced. The rubber reinforcement made from the additive has tension strength at break which is increased from 7.23MPa to 10.6MPa, even higher, and hardness from 76 to 82,.
Description
Technical field: [0001] The invention relates to the application of hematilite, in particular to the modified hematilite rubber reinforcing additive and its preparation method. Background technique: [0002] Stellerite is a mineral species in the zeolite family, its chemical composition (%): SiO 2 : 58.76, Al 2 o 3 : 14.13, CaO: 8.80, K 2 O: 0.11, Na 2 O: 0.18, Fe 2 o 3 : 0.44, H 2 o + : 16.87, H 2 o - : 1.25, natural staphilite is a kind of hydrous alkali metal or alkaline earth metal aluminosilicate mineral of natural zeolite. It is a framework silicate composed of silicon-oxygen tetrahedron and aluminum-oxygen tetrahedron. In addition, zeolite has a special structure, rich holes and channels, accounting for about 40-50% of the total volume, and has multiple uses. The applicant of this case once applied to the Chinese Patent Office on June 14, 2005 for the "preparation method of natural hematite as a rubber reinforcing additive". Carry out elutriation, pulveriz...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
IPC IPC(8): C09C1/40C09C3/00C08L21/00
Inventor 崔天顺陈南春
Owner GUANGXI NORMAL UNIV
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap