Method for preparing high machinery performance halogen-free anti-flaming PBT composite and composite material
A technology for composite materials and mechanical properties, applied in the field of polymer composite materials and their preparation, can solve the problems of low mechanical properties and low mechanical properties of halogen-free flame retardant materials, and achieve high mechanical properties, outstanding mechanical properties, and flame retardant properties. excellent effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0037] Embodiment 1: a kind of preparation method of high mechanical performance halogen-free flame-retardant PBT composite material, comprises the following steps:
[0038] (1) Weighing: See Table 1, weigh each raw material component according to the formula: PBT, ultrafine glass fiber, hindered phenol antioxidant, organic phosphite, toughening agent, flame retardant A, flame retardant Agent B, lubricant;
[0039] (11) Preparation of flame retardant B: after weighing hypophosphite and silane coupling agent, both are surface treated, and the specific operation steps are:
[0040] (a) Weigh the hypophosphite according to the formula, grind the hypophosphite for 1 to 10 hours, and then dry it;
[0041] (b) Place the dried hypophosphite in N 2 In an atmosphere, it is subjected to high-temperature treatment, repeated two or more times, and each time after high-temperature treatment is completed, it is cooled to room temperature;
[0042] (c) Pour the silane coupling agent onto ...
Embodiment 2
[0050] Embodiment 2: The preparation method and the composite material of the high-mechanical performance halogen-free flame-retardant PBT composite material provided by this embodiment are basically the same as in Embodiment 1, and the difference is that the screw diameter of the twin-screw extruder is 90mm, the ratio of screw length to diameter is set to 40, and the extrusion temperature is 260°C; the raw materials included in the composite material are the components and weight ratios listed in column 3 of Table 1.
Embodiment 3
[0051] Example 3: The preparation method and composite material of a kind of high mechanical performance halogen-free flame-retardant PBT composite material provided by this example are basically the same as Example 1, the difference is that the screw diameter of the twin-screw extruder The ratio of screw length to diameter is set to 38, and the extrusion temperature is 230°C; the raw materials included in this composite material are the components and weight ratios listed in column 4 of Table 1.
[0052] Table 1
[0053] raw material name
Example 1 (wt%)
Example 2 (wt%)
Example 3 (wt%)
polybutylene terephthalate
37.5
53.7
62.6
Ultrafine Glass Fiber
33
15
5
Hindered phenol antioxidant
0.2
0.4
0.5
Organic phosphite
0.3
0.2
0.5
Flame retardant A: Melamine phosphorus
salt
9
7
5
Flame retardant B: hypophosphite and
Compounds...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap