Atomic ash special for wood decoration

A kind of atomic ash and woodware technology, applied in the direction of filling slurry, etc., can solve the problems of complex atomic ash construction process, lack of convenient and fast construction, and damage to decorative coatings, and achieve convenient grinding, fast drying speed, and reduced usage. Effect

Inactive Publication Date: 2008-10-15
GUANGDONG SANVO CHEM IND TECH
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the common problem in wood coating is that the wood products are deformed due to the change of the water content of the wood substrate, especially the deformation and shrinkage of the substrate before and after the coating of large wooden furniture products, and during the substrate treatment process. damage the decorative coating
The existing atomic ash construction process is complicated, and it needs to be coated and ground many times
There is no putty specially used in the wood furniture production and decoration industry on the market, and there is also a lack of special putty products that are convenient and fast to construct

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach 1

[0038] The putty is composed of main ash and initiator, and the weight ratio of main ash and initiator is 100:2. The main ash is composed of the following components: 35 parts of unsaturated polyester resin and 5 parts of saturated polyester resin are put into the dispersion cylinder according to the weight ratio, and 0.005 parts of anti-skinning agent, 10 parts of styrene, 0.3 parts of accelerator and moisturizing agent are added. 0.2 part of wet agent, stirred at 600 r / min for 8 minutes; then add 1 part of thixotropic agent, 3 parts of zinc stearate and 5 parts of titanium dioxide and continue to stir at 600 r / min for 10 minutes; then Add 6 parts of barium sulfate, 26.495 parts of talc powder and 8 parts of atomic powder in turn, and then continue to stir for 15 minutes at a speed of 1100-1200 rpm; after passing the inspection, it is ground by a colloid mill and canned to make a finished product Main body grey. The initiator is composed of 50 parts of cyclohexanone peroxide...

Embodiment approach 2

[0040] The putty is composed of main ash and initiator, and the weight ratio of main ash and initiator is 100:2. The main ash is composed of the following components: 35 parts of unsaturated polyester resin and 5 parts of saturated polyester resin are put into the dispersion cylinder according to the weight ratio, and 0.005 parts of anti-skinning agent, 8 parts of styrene, 0.3 parts of accelerator and moisturizing agent are added. 0.3 part of wet agent, stirred for 8 minutes at 600 rpm; then added 1 part of thixotropic agent, 2 parts of zinc stearate and 5 parts of titanium dioxide, and continued stirring for 10 minutes at 600 rpm; then Add 7 parts of barium sulfate, 28.395 parts of talcum powder and 8 parts of atomic powder in turn, and then continue to stir for 15 minutes at a speed of 1100-1200 rpm; after passing the inspection, grind it with a colloid mill and then put it into a can to make a finished product Main body grey. The initiator is composed of 51 parts of methyl...

Embodiment approach 3

[0042] The putty is composed of main ash and initiator, and the weight ratio of main ash and initiator is 100:2. The main ash is composed of the following components: 35 parts of unsaturated polyester resin and 8 parts of saturated polyester resin are put into the dispersion cylinder according to the weight ratio, and 0.003 parts of anti-skinning agent, 8 parts of styrene, 0.3 parts of accelerator and moisturizing agent are added. 0.3 part of wet agent, stirred at 600 rpm for 5 minutes; then add 1 part of thixotropic agent, 1 part of zinc stearate and 5 parts of titanium dioxide and continue to stir for 13 minutes at 600 rpm; then Add 8 parts of barium sulfate, 25.397 parts of talc powder and 8 parts of atomic powder in turn, and continue stirring for 18 minutes at a speed of 1100-1200 r / min; after passing the inspection, it is ground through a colloid mill and canned to make a finished product Main body grey. The initiator is composed of 48 parts of cyclohexanone peroxide, 4...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a polymeric putty, in particular to an atomic ash specialized for carpentry decoration. The invention is specialized for meeting the using requirements of the carpentry furniture production and the interior decoration and fitment industry. The invention consists of two compositions: main ash and an evocating agent; the weight percentage of the main ash and the evocating agent is 100:2; when the invention is used, two compositions are evenly mixed according to mixture ratio. The main ash consists of the following compositions in percentage by weight: 35 to 45 portions of unsaturated polyester resin, 5 to 10 portions of saturated polyester resin, 0.003 to 0.005 portion of anti skinning agent, 8 to 12 portions of styrene, 0.3 to 1.2 portions of accelerant, 0.2 to 0.5 portion of wetting agent, 1 to 2 portions of thixotropic agent, 1 to 3 portions of zinc stearate, 5 to 8 portions of titanium pigment, 5 to 8 portions of permanent white, 20 to 35 portions of talcum powder and 8 to 12 portions of atomic powder. The evocating agent consists of the following compositions in percentage by weight: 45 to 55 portions of cyclohexanone peroxide or methyl ethyl ketone peroxide, 35 to 48 portions of dibutyl phthalate and 4 to 9 portions of SiO2. The atomic ash specialized for carpentry decoration has the following advantages that: the atomic ash has good adhesive force with various carpentry materials, good construction and flexility and shrinkage resistance and rapid drying speed and can fill up large holes or cracks; the putty film is exquisite, smooth and good in air-drying property and can be matched with wood lacquer in the market for use.

Description

Technical field: [0001] The invention relates to a special putty for woodware decoration. technical background: [0002] Putty is a kind of polymer putty with unsaturated polyester as the main body, and its trade name is putty. It is mainly used for caulking and filling the surface of metal and non-metallic materials before painting, in order to make the substrate smooth and smooth before painting, which is convenient for painting construction. With the continuous development of the domestic furniture coating and decoration industry, the requirements for the surface effect of furniture coating and the decoration and decoration of indoor woodware are also getting higher and higher. The appearance quality of products has attracted more and more attention of consumers, and high-quality coating indirectly puts forward higher and higher requirements for the treatment of substrates. Under the realistic circumstances of increasingly fierce competition among the same industry, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
Inventor 陈炳耀梁银生陈炳江陈绮文
Owner GUANGDONG SANVO CHEM IND TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap