Tourmaline plastic-based agglomerate material, production process thereof and pipes prepared from the material

A technology of tourmaline and masterbatch, which is applied in the field of plastic base materials and its production, can solve the problems of complicated installation, high cost, inability to satisfy ordinary users, etc., and achieve the effects of good purification effect, low cost and simple implementation.

Inactive Publication Date: 2008-11-26
施健 +1
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these devices are either costly or complicated to install, and cannot meet the needs of ordinary users.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

no. 2 Embodiment

[0014] In the second specific embodiment of the present invention, 45% of tourmaline, 2% of zirconia, 4% of zinc oxide, 2% of magnesium oxide, 3% of silicon oxide, 8% of cerium oxide, random copolymerized polypropylene (PP-R) 30%, toughening modifier M02 5%, filler modifier G02B 0.4%, filler modifier G02FX 0.6%, mix and stir with a mixer, put the mixed material into the filler port of the granulator, and heat to 250°C , until the material is melted, then the molten material is extruded by a granulator and stretched in a hot-melt state to form a tourmaline plastic base strip, and finally the plastic base strip is cooled for 2 minutes, and then enters the shearing machine to cut into a plastic base matrix grain. Then use the existing water pipe stretching technology to stretch the above-mentioned plastic-based masterbatch and PP-R material into a pipe. The inner layer of the pipe is a plastic-based masterbatch material layer, and the outer layer is a pressure-resistant and corro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
emissivityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a tourmaline plastic-based master batch material, which comprises a tourmaline, polypropylene random copolymer (PP-R), zirconia, magnesia, monox, rare earth compounds and a modifier; wherein, in the tourmaline, the content of the zirconia accounts for 3 percent to 6 percent, the content of the magnesia accounts for 2 percent to 5 percent, the content of the monox accounts for 10 percent to 20 percent, the content of the rare earth compounds accounts for 10 percent to 25 percent, the content of the modifier accounts for 5 percent to 8 percent and the content of the polypropylene random copolymer accounts for 10 percent to 30 percent. When the plastic-based master batch is prepared, all the materials are mixed, stirred, heated to be fused, overstocked and stretched into plastic-based stripes by a granulator and crushed. The tube stock manufactured by the plastic-based master batch material has a polypropylene random copolymer external layer and a tourmaline plastic-based master batch internal layer. The plastic-based master batch which is manufactured by mixing the tourmaline material and polypropylene can combine with other materials to manufacture the products with multi-function such as purification, healthcare, etc.

Description

technical field [0001] The invention relates to a plastic-based material and a production method thereof, in particular to a plastic-based material made of tourmaline and a pipe produced by using the material. Background technique [0002] Tourmaline is the general name of tourmaline minerals. Tourmaline has complex chemical composition. It is a silicate mineral with a ring structure of aluminum, sodium, iron, magnesium and lithium characterized by boron. Recent studies have shown that tourmaline has Many specific functions, mainly some health functions beneficial to the human body, so people began to develop products containing tourmaline, including various containers and textiles. At present, in the field of drinking water purification, the beneficial effect of tourmaline has also been confirmed. For example, tourmaline ceramic balls prepared by tourmaline will produce two kinds of negative ions (hydroxyl ion and hydronium ion) that are beneficial to the human body. In add...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08K3/34
Inventor 秦荣
Owner 施健
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products