Preparation method for magnesium alloy cast paint
A technology for casting coatings and magnesium alloys, applied in casting molding equipment, metal processing equipment, coatings, etc., can solve problems such as hot cracking of magnesium castings, and achieve the effects of preventing oxidation, strong heat preservation, and smooth surface
Inactive Publication Date: 2009-01-14
ZHONGHONG (TIANJIN) IND CO LTD
View PDF0 Cites 8 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] At present, the coatings used in the production of magnesium alloys are mostly borrowed from aluminum alloy coatings, and there are very few special coatings, and magnesium castings often produce hot cracks during use.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment
[0006] Embodiment: a kind of preparation method of magnesium alloy casting paint, 0.8% palygorskite clay is mixed with 17% water and grinds for 3 hours, makes first liquid; Then 3% talcum powder, 4% diatomite, 0.6 Put %NH4BF4 and 3% boric acid into the ball mill, add liquid A, 4% silica sol and 67.6% water and grind for 3 hours to get magnesium alloy metal mold casting coating, heat the metal mold to about 200 ℃ and spray it on the metal mold The surface is coated with a layer of magnesium alloy casting paint, and it can be dried after drying.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The present invention relates to a method for preparing the magnesium casting coating; 0.8 percent paligorskite clay that is configured with 17 percent of water is milled for 3 hours to be made into solution A; secondly 3 percent of talcum powder, 4 percent of diatomite, 0.6 percent of NH4BF4 and 3 percent of boric acid are put into a spherical mill, and is respectively mixed with solution A, 4 percent of silica sol and 67.6 of percent water to be milled for 3 hours to obtain the magnesium alloy metal-typed casting coating; metal mould is heated to be about 200 DEG C, and then is sprayed with a layer of magnesium alloy casting coating on the surface, and is dried finally. The method of the present invention has the advantages of strong heat preservation, flame retardant performance, sticking performance and coating performance, favorable suspension performance and less heat fracture of the casting piece. Oxidation is prevented, so the surface is bright and smooth and is free from oxidized wrinkle.
Description
technical field [0001] The invention relates to a preparation method of magnesium alloy casting paint. Background technique [0002] At present, most of the coatings used in the production of magnesium alloys are borrowed from aluminum alloys, and there are very few special coatings, and magnesium castings often produce hot cracks during use. Contents of the invention [0003] The object of the present invention is to overcome the above-mentioned deficiencies, and propose a method for preparing magnesium alloy casting paint, which has excellent flame retardancy, heat preservation, adhesion and coating properties, no thermal cracking, smooth surface, and no oxidation wrinkle. [0004] The technical scheme of the present invention is: a kind of preparation method of magnesium alloy casting coating, it is characterized in that: 0.8% palygorskite clay is mixed with 17% water and grinds for 3 hours, makes first liquid; Then 3% talcum powder, Put 4% diatomaceous earth, 0.6% NH4...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): B22C3/00
Inventor 张云波
Owner ZHONGHONG (TIANJIN) IND CO LTD