Annealing process of titanium foil or strip

An annealing process, a technology of titanium foil, applied in the field of metal material processing, can solve the problems of insufficient stability of product quality and insufficient annealing, and achieve the effects of good stress removal effect, thorough annealing, and stable product quality

Inactive Publication Date: 2009-01-28
常荣波
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the annealing of rare and precious metals such as titanium foil or strip, it is generally considered that the temperature should not exceed 550°C, but in practice, it has been found that the annealing of titanium materials annealed at this temperature is not thorough enough, resulting in unstable product quality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1: will need annealing material to be put into vacuum annealing furnace, and vacuum degree reaches 10 -7 Above, then heat up, keep warm at 560±5°C for 2-4 hours, and finally cool down to room temperature to take out the material.

Embodiment 2

[0013] Embodiment 2: will need annealing material to be put into vacuum annealing furnace, and vacuum degree reaches 10 -7 Above, and then heat up, keep warm at 610±5°C for 2-4 hours, and finally cool down to room temperature to take out the material.

Embodiment 3

[0014] Embodiment 3: will need annealing material to be put into vacuum annealing furnace, vacuum degree reaches 10 -7 Above, and then heat up, keep warm at 630±5°C for 2-4 hours, and finally cool down to room temperature to take out the material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention pertains to a titanium foil material or belt material annealing technology in the technical field of metal processing, which is carried out according to the steps as follows: (1) materials are put in a vacuum annealing furnace, with vacuumization degree up to above 10 to 7; (2) the materials are heated to 560 DEG C to 700 DEG C with heat insulation for 2 hours to 4 hours; and (3) the temperature is lowered to room temperature and the materials are taken out. The annealing technology of the invention has the advantages of thorough annealing, good effect on removing stress and stable product quality and overcomes the defect that presently, when titanium foil materials are annealed, the annealing under comparatively low temperature is not thorough enough, which results in that the product quality is not stable enough.

Description

technical field [0001] The invention belongs to the technical field of metal material processing, especially the processing of rare and precious metals. Background technique [0002] Annealing is a commonly used method in metal material processing. In the annealing of rare and precious metals such as titanium foil or strip, it is generally considered that the temperature should not exceed 550°C, but it has been found in practice that the annealing of titanium materials annealed at this temperature is not thorough enough, resulting in unstable product quality. Contents of the invention [0003] The object of the present invention is to provide an annealing process for titanium foil or strip, so as to achieve thorough annealing and improve the product quality stability of titanium foil. [0004] Specifically, the annealing process of titanium foil or strip material is implemented according to the following steps: [0005] (1), put the material into the vacuum annealing fur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22F1/18
Inventor 常荣波
Owner 常荣波
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com