Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Steel for hot-rolled low carbon punching and producing method thereof

A production method and technology of final rolling temperature, applied in the field of hot-rolled low-carbon stamping steel and its production method, can solve the problems of low-carbon steel with low elongation and low elongation, and achieve low cost, high elongation, Effects that are less difficult to control

Inactive Publication Date: 2011-01-05
PANGANG GROUP RESEARCH INSTITUTE CO LTD +3
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the elongation of the steel is low (about 35%), it is difficult to meet the needs of higher elongation low carbon steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

Embodiment 2

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
elongationaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to hot rolling low-carbon stamping steel and a manufacturing method thereof, belonging to the field of metallurgy. The technical problem the invention aims at solving is to provide a hot rolling low-carbon stamping steel with specific elongation A50 being more than or equal to 45% and a manufacturing method thereof. The weight percentages of the chemical components of the low-carbon stamping steel of the invention are as follows: C: 0.03-0.07%, Mn: 0.20-0.35%, Als: 0.015-0.08%, Ti: 0.004-0.020%, N: less than or equal to 0.0040%, Ti / N: less than or equal to 3.43, Cr: 0.40-0.60%, and the balance of Fe and unavoidable impurities. The low-carbon stamping steel of the invention can be rolled at relatively low finishing temperature, and has the advantages of low yield strength, high specific elongation and no generation of macrocrystal at the surface of strip steel, thus being applicable to various spare parts which need stamping for moulding.

Description

Hot-rolled low-carbon stamping steel and production method thereof technical field The invention relates to hot-rolled low-carbon stamping steel and a production method thereof, belonging to the field of metallurgy. Background technique In recent years, with the wide application of hot-rolled low-carbon stamping steel in construction, automobile and other industries, the research on the chemical composition and hot-rolling process of hot-rolled low-carbon stamping steel has also made great progress. There are related reports about changing the properties of hot-rolled low-carbon stamping steel by changing the chemical composition or hot-rolling process of hot-rolled low-carbon stamping steel. For example, the patent application with application number 200510012895.1 discloses a low-carbon steel rolled by ferrite process. The chemical composition of the steel is: C: 0.01~0.06%, Mn≤0.40%, S≤0.01%, P ≤0.03%, Si≤0.04%, Al: 0.01-0.05%, the balance is Fe and unavoidable impuri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/28C21D8/04
Inventor 李军王平利刘勇尤秀妆李正荣
Owner PANGANG GROUP RESEARCH INSTITUTE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com