Compound type concrete foaming agent, preparation method and application thereof

A technology for concrete and foaming agent, applied in the field of building materials, can solve the problems of decreased flexural strength, failure to meet engineering requirements, delayed setting, etc., and achieve the effects of increasing the amount of foaming, low price, and easy availability of raw materials

Inactive Publication Date: 2010-02-24
刘兴山
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Practice has proved that for every 1% increase in foaming air content, the compressive strength of concrete will decrease by about 5%, and the flexural strength will decrease by 2%-3%.
The strength of foam concrete is too low or does not meet the engineerin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compound type concrete foaming agent, preparation method and application thereof
  • Compound type concrete foaming agent, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] The present invention will be further described in conjunction with the following examples. It should be understood that these examples are only for illustrative purposes and in no way limit the protection scope of the present invention.

[0019] The implementation mode of the composite foaming agent is described by the ratio of each raw material and the text in Table 1, and its weight unit is calculated by heart:

[0020] Table 1

[0021]

[0022]

[0023] Taking Example 2 as an example, the method for preparing the composite concrete foaming agent of the present invention is as follows:

[0024] Weigh the raw materials according to Table 1, take 54.65kg of water, heat it with 30% of the water to 70-80°C and dilute the polyvinyl alcohol for use; put the remaining water in a heated container, and process 4kg of industrial caustic soda; Add 20kg of rosin, pyrolyze at 70-80℃ while stirring. After the raw materials are fully dissolved, cool to room temperature for about 100 minute...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a compound type concrete foaming agent, a preparation method and an application thereof. The compound type concrete foaming agent is prepared by compounding a component A and acomponent B, wherein the component A comprises 10-20 parts of polyvinyl alcohol, 15-25 parts of colophony, 1.5-2.5 parts of anhydrous sodium carbonate, 3.5-4.5 parts of industrial sodium hydroxide, 3-5 parts of triethanolamine, 0.2-0.5 parts of industrial grade hydrochloric acid and 53.5-55.8 parts of water; and the component B comprises 0.2-0.5 parts of triethanolamine, 8-10 parts of sodium sulfate, 12-15 parts of sodium nitrite, 10-25 parts of calcium chloride and 54.7-64.5 parts of water. The compound type concrete foaming agent not only can increase the doped quantity of the foaming agentbut also can compensate the concrete strength and the solidification time; the compound type concrete foaming agent can be used for manufacturing foam concrete with super-low capacity, also utilize alarge amount of waste residues, such as industrial and architectural rubbish and the like, to produce light foamed concrete.

Description

technical field [0001] The invention belongs to the field of building materials, and relates to a composite concrete foaming agent and its preparation method and application, in particular to a foaming agent that can increase the amount of foaming agent and compensate the strength and solidification time of concrete. It is a composite foaming agent for producing ultra-low-capacity foamed concrete, and a large amount of waste residues such as industrial and construction waste can be used to produce lightweight foamed concrete. Background technique [0002] To prepare lightweight foamed concrete, it is first necessary to prepare a foaming agent with a large amount of foam and strong foam stabilizing ability. After foaming by mechanical means, it is mixed with concrete and cast into shape. The lightweight foamed (or foamed) concrete produced by the foaming agent is a porous material with a porosity of up to 85% and a thermal conductivity of 0.15-0.21 / (m.k). At present, there a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B24/34
CPCC04B28/10C04B2103/0006C04B40/0046
Inventor 刘兴山靳雪征刘冰
Owner 刘兴山
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap