Method and device for producing water tap by using colored glaze

A water faucet and glass technology, applied in glass forming, glass manufacturing equipment, manufacturing tools, etc., can solve the problems of surface atomization, limited profit, peeling of electroplating layer, etc., and achieve smooth surface, high added value, and high aesthetics sexual effect

Inactive Publication Date: 2010-07-21
明本企业有限公司
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Generally, the water supply faucet is made of copper and cast. However, the surface of the copper product must be electroplated after completion to make it have a bright surface. However, the bright surface is eroded by scale for a long time, resulting in surface fog. However, after a period of time, the previous bright surface cannot be restored, and even the electroplating layer peels off, and due to the large number of products in the market and their sales competition, the profit is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method and device for producing water tap by using colored glaze
  • Method and device for producing water tap by using colored glaze
  • Method and device for producing water tap by using colored glaze

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] see Figure 1 to Figure 8 Shown, be the preparation method of the present invention, its step comprises:

[0053] a. A wax mold 2 is formed by pouring wax into the soft silicone wax injection mold 1 (such as figure 2 );

[0054] b. The wax mold 2 is then placed in a plaster mold 3 and filled with a plaster cast mold to form a plaster mold 31 of the main body of the flow channel and pipeline body covered with a layer of the wax mold 2 (such as Figure 4 );

[0055] c. heating the wax-melting equipment 4 at high temperature again, so that the wax pattern 2 flows out after melting in the main body plaster mold 31 of the runner pipeline, and a hollow is formed in the plaster mold 31 of the main body of the runner pipeline (such as Figure 5 );

[0056]d. the plaster mold 31 of the main body of the aforementioned runner pipeline (such as Figure 6 ) and then placed in the molding die 5 ( Figure 7 ), so that there is a reserved gap and space between the plaster mold 3...

Embodiment 2

[0063] see figure 1 , Figure 7 ~ Figure 10 Shown, be the preparation method of the present invention, its step comprises:

[0064] a. prefabricating the main body 3' of the stainless steel runner pipeline with a stainless steel material;

[0065] b. impregnating the gypsum layer 3" with the stainless steel flow channel main body 3' again to form a gypsum layer covering the stainless steel flow channel main body 30 (such as Figure 9 );

[0066] c. directly place in the forming mold 5 after being solidified (such as Figure 7 );

[0067] d. The aforementioned gypsum layer coats the main body 30 of the stainless steel runner pipeline, and then places it in the forming mold 5, and places the forming mold 5 in a heating furnace 6 (such as Figure 8 );

[0068] e. Glass particles A are placed in the heating furnace 6, and the glass A is melted into liquid glass A' by heating, and slowly dripped into the forming mold 5 to fill the gypsum layer and coat the stainless steel flo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method and a device for producing water taps by using colored glaze. Mould wax is poured into a flexible silicon rubber mould to form a wax mould. The wax mould is placed in a gypsum mould and gypsum is poured into the gypsum mould to cast a mould. A gypsum layer covers the external surface of the wax mould. Through high-temperature heating, the wax mould is molten to obtain a runner pipeline main body gypsum mould. The runner pipeline main body gypsum mould is put into a forming mould. Liquid colored glaze is slowly dripped into the forming mould to fill gaps between the runner pipeline main body gypsum mould or a steel runner pipeline main body covered by the gypsum layer and the forming mould and the reserved space. After cooling, the forming mould is taken out and the colored glaze water tap main body blank is obtained. The runner pipeline main body gypsum mould in the colored glaze water tap main body blank is destroyed to obtain a colored glaze water tap main body. Finally, through surface processing, the colored glaze water tap main body can be assembled with other components to form a colored glaze water tap. The colored glaze water tap has the advantages of beautiful appearance and high added value.

Description

technical field [0001] The present invention relates to a method for making a water supply faucet and its device, especially the gap and reserved space between the gypsum mold of the main body of the flow channel pipeline or the gypsum layer coated stainless steel flow channel pipeline body and the forming mold by using colored glass. To form the technical field of the main body of the glazed faucet. Background technique [0002] Generally, the water supply faucet is made of copper, which is casted. However, the surface of the copper product must be electroplated after completion to make it have a bright surface. However, the bright surface is eroded by scale for a long time, resulting in surface fog. However, after a period of time, the previous bright surface cannot be restored, and even the electroplating layer peels off, and due to the large number of products in the market and their sales competition, the profit is limited. Contents of the invention [0003] Aiming a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03B19/02
Inventor 林汉滨林佑伦
Owner 明本企业有限公司