Method for plating chrome on surface of thin plate

A technology of surface chrome plating and thin plate, applied in the field of chrome plating on the surface of thin plate, can solve the problems of high environmental protection emission pressure, high investment and high production cost

Active Publication Date: 2012-12-12
BAOSHAN IRON & STEEL CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] Although the two-step method can control the amount of metal chromium and chromium oxide more accurately, it will not affect the corrosion resistance of the chrome-plated plate after processing and deformation due to too much metal chromium, or too much chromium oxide will darken the surface color and affect the Appearance; but the investment and production costs are relatively high, and the pressure on environmental protection and emissions is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for plating chrome on surface of thin plate
  • Method for plating chrome on surface of thin plate
  • Method for plating chrome on surface of thin plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0099] Concrete steps and process parameters of the embodiments of the present invention are as follows:

[0100] 1. Alkaline washing

[0101] Such as figure 2 As shown, the equipment makes the strip pass through the solution to remove the oil and dirt adhering to the surface of the strip. It includes a pre-soak tank 1, which soaks the strip for preliminary degreasing; The electrodes on both sides of the middle strip are used for degreasing; one scrubbing tank 3 is used for physical degreasing; two rinsing tanks 4 are sprayed with high-temperature water to remove the lye on the surface of the strip.

[0102] 1. Alkali leaching

[0103] Alkali concentration: active alkali 35g / l

[0104] Solution temperature: 45°C

[0105] Additive: Electrolytic cleaning additive 25 (low temperature cleaning agent);

[0106] 2. Electrolytic cleaning

[0107] Liquid: active alkali

[0108] Temperature: 45°C

[0109] Concentration: 35g / L

[0110] Power supply: 8.0KA, 30V, 2 sets

[0111...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
current efficiencyaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for plating chrome on a surface of a thin plate. The method comprises the following steps: 1) alkali washing, including alkali liquor leaching, electrolysis washing and alkali washing; 2) pickling, including electrolysis pickling and acid washing; 3) electroplating, including chromeplating and washing; and 4) oiling. The method sufficiently utilizes the performance advantage of CrO3+NH4 plating solution, optimizes the pre-treatment pickling process and electroplating parameters, particularly controls the solution concentration of alkali washing and pickling, strictly controls the current efficiency of an electroplating section and the electroplating concentration, overcomes the defects in the tradition process, generates compact metal chrome and chromic oxide layers on the surface of strip steel, realizes one-step production of an electrolytic chromium steel plate the strip steel surface of which is plated with optimally combined metal chromium and chromic oxide so as to obtain the excellent chromeplated plate with bright and uniform plating layer. Meanwhile, the method saves energy consumption, reduces pressure environment-friendly emission, reduces cost for production and maintenance, and creates a condition for improving the chromeplated plate, thus having excellent popularization and application prospect.

Description

technical field [0001] The invention relates to a treatment method for chrome plating on the surface of a steel plate, in particular to a method for chrome plating on the surface of a thin plate. Background technique [0002] For more than 100 years, tin-plated steel has been the main packaging material such as can container materials and shells. The current annual output of the world is about 20 million tons. Tin-free steel plate" instead of tin plate. [0003] At the beginning of research on other surface-treated thin steel plates, most of them were "conversion coatings", that is, to produce chemical conversion layers on the iron surface in aqueous solution, and trial-produced chromic-acid-treated steel plates and electrolytic phosphate-treated steel plates. Nickel steel plate, vacuum aluminum plated steel plate, etc. Compared with electroplated tin plate, these materials have insufficient corrosion resistance, the process time is much longer than tin plating time, and th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C25D3/04C25D5/34C25D5/48C23G1/02C23G1/14C23F17/00C25F1/04
Inventor 王文朱国和矫大鹏
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com