Sand textured two-component plaster mortar composition

A plastering mortar, two-component technology, applied in the field of construction mortar, to achieve the effect of strengthening force, improving mechanical and physical properties, and excellent spraying effect

Active Publication Date: 2012-11-07
苏州盛泽科技创业园发展有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current market products and patent searches have not found a sand wall-like coating that is used in conjunction with polyurethane emulsion and inorganic adhesives

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sand textured two-component plaster mortar composition
  • Sand textured two-component plaster mortar composition
  • Sand textured two-component plaster mortar composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] 20 parts of white cement, 60 parts of corundum, 0.5 parts of gelatin powder, 0.3 parts of xanthan gum, 0.1 part of hydroxyethyl cellulose ether, 3 parts of lithopone, 0.1 part of magnesium fluorosilicate, 1.5 parts of polytetrafluoroethylene micropowder , 0.1 part of sodium tripolyphosphate, 0.1 part of defoamer, 40 parts of modified polyurethane emulsion, and 1 part of dipropylene glycol methyl ether.

[0036] At room temperature, add white cement, carborundum, cellulose ether, lithopone, flame retardant, sodium tripolyphosphate, hardener and defoamer into the mixer and stir evenly. Before use, add modified Polyurethane Emulsion and Dipropylene Glycol Methyl Ether.

[0037] The preparation method of described modified polyurethane emulsion is as follows:

[0038] (1) Heat 100 parts by weight of silica powder to 110°C, spray 2 parts by weight of molten polyethylene wax on the silica powder, and after mixing, spray 3 parts by weight of glycidoxypropyl Coupling of trime...

Embodiment 2

[0046] 22 parts of white cement, 55 parts of corundum, 0.7 parts of gelatin powder, 0.3 parts of xanthan gum, 0.15 parts of hydroxyethyl cellulose ether, 4 parts of lithopone, 0.2 parts of magnesium fluorosilicate, 2 parts of polytetrafluoroethylene micropowder , 0.2 parts of sodium tripolyphosphate, 0.2 parts of defoamer, 42 parts of modified polyurethane emulsion, and 1.5 parts of dipropylene glycol methyl ether.

[0047] At room temperature, add white cement, carborundum, cellulose ether, lithopone, flame retardant, sodium tripolyphosphate, hardener, P803 defoamer into the mixer and stir evenly, then add modified Polyurethane Emulsion and Dipropylene Glycol Methyl Ether.

[0048] The preparation method of described modified polyurethane emulsion is as follows:

[0049] (1) Heat 100 parts by weight of silica powder to 110°C, spray 3 parts by weight of molten polyethylene wax on the silica powder, and after mixing, spray 4 parts by weight of glycidoxypropyl Coupling of trim...

Embodiment 3

[0057] 24 parts of white cement, 50 parts of corundum, 0.9 parts of gelatin powder, 0.25 parts of xanthan gum, 0.2 parts of hydroxyethyl cellulose ether, 5 parts of lithopone, 0.3 parts of magnesium fluorosilicate, 2.5 parts of polytetrafluoroethylene powder , 0.3 parts of sodium tripolyphosphate, 0.3 parts of defoamer, 44 parts of modified polyurethane emulsion, and 2 parts of dipropylene glycol methyl ether.

[0058] At room temperature, add white cement, carborundum, cellulose ether, lithopone, flame retardant, sodium tripolyphosphate, hardener, P803 defoamer into the mixer and stir evenly, then add modified Polyurethane Emulsion and Dipropylene Glycol Methyl Ether.

[0059] The modified polyurethane emulsion was prepared by the method of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
activation indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a sand textured two-component plaster mortar composition. The composition consists of the following components in parts by weight: 20 to 30 parts of white cement, 40 to 60 parts of silicon carbide, 0.5 to 1.5 parts of gelatin powder, 0.1 to 0.3 part of xanthan gum, 0.1 to 0.2 part of cellulose ether, 3 to 7 parts of lithopone, 1.5 to 3 parts of fire retardant, 0.1 to 0.5 part of sodium tripolyphosphate, 0.1 to 0.5 part of hardening agent, 0.1 to 0.3 part of defoaming agent, 40 to 50 parts of modified polyurethane emulsion, and 1 to 3 parts of dipropylene glycol methyl ether. A filmed polyurethane adhesive film has hydrophobic nature better than an adhesive film copolymerized from pure acrylic acid, styrene-acrylate or vinyl acetate, so that the mortar spraying effect is excellent, and the effect of simulating stones rivals that of stones; and the composition has good effects in adhesive strength, water resistance, stain resistance, light and weather resistance.

Description

technical field [0001] The invention relates to a construction mortar. Background technique [0002] With the rapid development of my country's economy and the continuous improvement of people's living standards, the development of modern high-end residential buildings, commercial buildings, and new public building facilities in China has entered a new period. People pay more attention to beautifying the environment while meeting material needs. The requirements of high-end residential buildings, commercial buildings, and new public buildings put forward higher requirements for aesthetics, high quality, and environmental protection. Sand wall-like mortar is a new type of exterior material because of its simulated stone effect and Reliable quality, convenient operation and economic benefits have been valued. However, the sand wall-like coatings currently used in the market, the adhesives are mainly polymer resins or emulsions such as pure acrylic, styrene-acrylic or vinyl acet...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04
CPCC04B28/02
Inventor 施晓旦郭和森
Owner 苏州盛泽科技创业园发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com