Low surface energy polyester film and preparation method and application thereof

A low surface energy, polyester film technology, applied in chemical instruments and methods, synthetic resin layered products, layered products, etc. Composite and other issues to achieve the effect of meeting food hygiene requirements, simple structure, and low cost

Active Publication Date: 2011-10-19
ORG TECH CO LTD
View PDF10 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The polyester film mainly considers high temperature transfer and optical properties. The polyester in the raw material is not modified, resulting in too high melting point and relatively fast crystallization speed during processing. Subsequent processing, in addition, both surfaces of the film contain ethylene bis-lauramide

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low surface energy polyester film and preparation method and application thereof
  • Low surface energy polyester film and preparation method and application thereof
  • Low surface energy polyester film and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0058] Example one

[0059] figure 1 It is a schematic cross-sectional view of the first embodiment of the present invention.

[0060] Such as figure 1 It can be seen that the low surface energy polyester film obtained in this embodiment has a two-layer structure, wherein one layer is a modified polyester layer and the other layer is a low surface energy polyester layer.

[0061] Firstly, the raw materials are mixed into modified polyester bright slices, inorganic additive slices and low surface energy additive slices, and they are dried on a boiling bed at a drying temperature of 150°C and a drying time of 4 hours.

[0062] Modified polyester bright slices include: isophthalic acid modified polyethylene terephthalate (the molar content of isophthalic acid is 10%); modified polyester bright slices have been tested Its melting point is 210℃~240℃, and its glass transition temperature is 60℃~80℃.

[0063] Inorganic additive chips include: SiO 2 The mass fraction of the powder is 2300 ppm,...

Example Embodiment

[0071] Example two

[0072] figure 2 It is a schematic cross-sectional view of the second embodiment of the present invention.

[0073] Such as figure 2 It can be seen that the low surface energy polyester film of this embodiment has a three-layer structure, in which two layers are modified polyester layers, and the other layer is a low surface energy polyester layer.

[0074] Firstly, the raw materials are mixed into modified polyester bright slices, inorganic additive slices and low surface energy additive slices, and they are dried on a boiling bed at a drying temperature of 150°C and a drying time of 4 hours.

[0075] Modified polyester bright slices include: isophthalic acid modified polyethylene terephthalate (the molar content of isophthalic acid is 13%); modified polyester bright slices have been tested The melting point is 210℃~240℃.

[0076] Inorganic additive chips include: SiO 2 The mass fraction of the powder is 2000 ppm, and the rest is isophthalic acid modified polye...

Example Embodiment

[0083] Example three

[0084] The low surface energy polyester film of this embodiment has a three-layer structure, in which two layers are modified polyester layers, and the other layer is a low surface energy polyester layer.

[0085] Firstly, the raw materials are mixed into modified polyester bright slices, inorganic additive slices and low surface energy additive slices, and they are dried on a boiling bed at 120°C for 4 hours.

[0086] Modified polyester bright slices include: isophthalic acid modified polyethylene terephthalate (the molar content of isophthalic acid is 16%); modified polyester bright slices have been tested Its melting point is 200℃~240℃, and its glass transition temperature is 60℃~80℃.

[0087] Inorganic additive chips include: SiO 2 The mass fraction of the powder is 2500 ppm, and the rest is isophthalic acid modified polyethylene terephthalate (the molar content ratio of isophthalic acid is 16%).

[0088] The low surface energy additive chip includes: 4% by w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Melting pointaaaaaaaaaa
Glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low surface energy polyester film and a preparation method and application thereof. One side of the low surface energy polyester film is a modified polyester layer, and the other side is a low surface energy polyester layer, wherein the modified polyester layer comprises the following components in percentage by weight: 300 to 5,000ppm of antiblocking agent, and the balance of modified polyester; the low surface energy polyester layer comprises the following components in percentage by weight: 90 to 99.9 percent of modified polyester, 0.1 to 10 percent of low surface energy additive, and 300 to 5,000ppm of antiblocking agent. The low surface energy polyester film is simple in structure, scientific in formula and simple and convenient in preparation method, overcomes lots of defects of the prior art, has the advantages of safety, sanitation, corrosion resistance, no conglutination to packaged contents and tight connection with a metal base material, and can be widely applied to metal can food packing industry.

Description

technical field [0001] The invention relates to film technology, in particular to a low-surface-energy polyester film used in the metal packaging industry for bonding on the surface of a metal substrate, its preparation method and application. Background technique [0002] The metal can food packaging industry requires that the surface of the inner wall in contact with the contents of the package should be below 34 dynes for luncheon meat, fish and tomato sauce, so that the filled contents can be easily dumped. At present, the inner wall of metal cans is mainly coated with paint. After curing, the paint is hard and brittle. The paint has poor ductility and impact resistance. The metal plate coated with it cannot be processed with large deformation, so the deformation is relatively large. The two-piece can is usually sprayed after the metal can is formed, and the spraying process after forming is relatively complicated, resulting in an increase in cost. In addition, although...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/36B32B27/18
Inventor 赵宇晖叶强曾科
Owner ORG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap