Water and oil repellent finishing method for bag type dedusting material

A technology of water and oil repellency and bag dust removal, which is applied in separation methods, chemical instruments and methods, fiber treatment, etc., and can solve problems such as unsatisfactory water and oil repellency effects

Active Publication Date: 2012-11-14
江苏东方滤袋股份有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention is to provide a water-repellent and oil-repellent finishing method for bag-type dust removal materials in view of the above-mentioned deficiencies. The problem of unsatisfactory oil repellency aims to provide a finishing method for improving the water and oil repellency of the soot filter material, and to improve the water and oil repellency of the soot filter material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water and oil repellent finishing method for bag type dedusting material
  • Water and oil repellent finishing method for bag type dedusting material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] 1. Preparation of finishing agent: PTFE emulsion, benzyl silicone oil emulsion, alcohol, Tween (detergent), glycerin, hardening agent, resin HA, adhesive and water are selected as the finishing agent, and the quality of the material is 100%. Compare:

[0031] PTFE emulsion 5 Kg ( 5 %)

[0032] Adhesive 12 Kg (12 %)

[0033] Resin HA 2 Kg (2 %)

[0034] Hardener 2 Kg (2 %)

[0035] Benzyl silicone oil emulsion 2 Kg (2 %)

[0036] Alcohol 4 Kg (4 %)

[0037] Glycerol 0.8 Kg (0.8 %)

[0038] Tween (detergent) 2.2 Kg (2.2%)

[0039] Water 70 Kg (70 %)

[0040] Weigh the above-mentioned materials according to the mass percentage distribution ratio and put them into the mixing container, stir and mix evenly, prepare the finishing agent, and set aside;

[0041] Wherein the resin HA is a cross-linked acrylic resin; the hardening agent is a polyethylene polyamine resin; the adhesive is a fluorine-containing acrylic resin;

[0042] Described PTFE emulsion is polytetraflu...

Embodiment 2

[0047] 1. Preparation of finishing agent: PTFE emulsion, benzyl silicone oil emulsion, alcohol, Tween (detergent), glycerin, hardening agent, resin HA, adhesive and water are selected as the finishing agent, and the quality of the material is 100%. Compare:

[0048] PTFE emulsion 9.4Kg (9.4 %)

[0049] Adhesive 6 Kg (6 %)

[0050] Resin HA 1 Kg (1 %)

[0051] Hardener 0.5 Kg (0.5 %)

[0052] Benzyl silicone oil emulsion 0.6 Kg (0.6 %)

[0053] Alcohol 1.5 Kg (1.5 %)

[0054] Glycerol 0.2 Kg (0.2 %)

[0055] Tween (detergent) 0.8 Kg (0.8 %)

[0056] Water 80 Kg (80 %)

[0057] Weigh the above-mentioned materials according to the mass percentage distribution ratio and put them into the mixing container, stir and mix evenly, prepare the finishing agent, and set aside;

[0058] The chemical name of the resin HA is cross-linked acrylic resin; the chemical name of the hardening agent is polyethylene polyamine resin; the chemical name of the adhesive is fluorine-containing ac...

Embodiment 3

[0064] 1. Preparation of finishing agent: PTFE emulsion, benzyl silicone oil emulsion, alcohol, Tween (detergent), glycerin, hardening agent, resin HA, adhesive and water are selected as the finishing agent, and the quality of the material is 100%. Compare:

[0065] PTFE emulsion 10 Kg (10 %)

[0066] Adhesive 8 Kg (8 %)

[0067] Resin HA 1.5Kg (1.5%)

[0068] Hardener 1.5 Kg (1.5 %)

[0069] Benzyl silicone oil emulsion 1.5 Kg (1.5 %)

[0070] Alcohol 3 Kg (3 %)

[0071] Glycerol 0.5 Kg (0.5 %)

[0072] Tween (detergent) 2.5 Kg (2.5%)

[0073] Water 71.5Kg (71.5%)

[0074] Weigh the above-mentioned materials according to the mass percentage distribution ratio and put them into the mixing container, stir and mix evenly, prepare the finishing agent, and set aside;

[0075] Wherein the resin HA is a cross-linked acrylic resin; the hardening agent is a polyethylene polyamine resin; the adhesive is a fluorine-containing acrylic resin;

[0076] Described PTFE emulsion is p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water and oil repellent finishing method for a bag type dedusting material and relates to a material finishing method for high-temperature gas treatment of steel works, industrial furnaces, and industrial boilers. The finishing method comprises the following steps of: (1) preparing a finishing agent, namely weighing polytetrafluoroethylene (PTFE) emulsion, polymethylphenyl siloxane fluid emulsion, alcohol, Tween, glycerol, a hardening agent, resin HA, and adhesive and water in a mass ratio and placing in a container, stirring and mixing uniformly, and thus obtaining the finishing agent for later use; (2) padding the dedusting material by using the prepared finishing agent by a padding machine, wherein the pressure of a rotary drum of a compression roller during padding of the dedusting material is 0.5 to 0.7 MPa, and the speed of the rotary drum is 3.5 to 5.5 m / min; (3) allowing the padded dedusting material to pass through a drying oven, wherein the drying temperature is 140 to 190 DEG C, and the travel speed of the dedusting material in the drying oven is 3.5 to 5.5 m / min; and after the dedusting material is dried, winding the dried dedusting material on a fabric roller to finish the water and oil repellent finishing work of the bag type dedusting material.

Description

technical field [0001] The present invention relates to a water-repellent and oil-repellent finishing method for bag-type dedusting materials, which relates to a material finishing method for high-temperature gas treatment in steel mills, industrial furnaces, and industrial boilers, specifically, a kind of bag-type dedusting materials Water and oil repellent finishing method. Background technique [0002] In the field of filter materials, bag filter is a common cleaning method for online cleaning. In the working condition of the bag filter, the mixed gas of steam, oil gas and other acidic and alkaline gases is often encountered. This mixed gas often has strong acid and strong alkalinity, and the filter material that has not been treated with water and oil repellency will absorb The mixed gas will cause the material to be corroded and its strength will decrease; while the surface tension of the filter material treated with water and oil repellency increases, the mixed gas i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/256D06M15/277D06M15/263B01D46/02
Inventor 张之荣张旭东咸将
Owner 江苏东方滤袋股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products