High-temperature-resistant maleic anhydride (MAH) resin catalyst and preparation method thereof

A technology of maleic anhydride and high temperature resistance is applied in the field of high temperature resistant maleic anhydride resin catalyst and its preparation, which can solve the problem of limiting the use range of ion exchange resin catalyst, easy isomerization of products into dimethyl fumarate, and the existence of free radicals in finished products. S and other problems, to achieve the effect of good catalytic effect, high temperature resistance and high selectivity

Active Publication Date: 2012-01-18
KAIRUI ENVIRONMENTAL PROTECTION TECH
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional method of producing DMM is to use maleic anhydride as raw material, and carry out esterification reaction with methanol under the catalysis of sulfuric acid. Although this production process has high catalytic activity and low price, there are many side reactions and the product is easy to isomerize. Fushun Petrochemical Research Institute (FRIPP) has successfully developed maleic anhydride and methanol under the action of a solid acid catalyst through a lot of experimental work based on the above

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant maleic anhydride (MAH) resin catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] 1). Polymerization reaction

[0053] In the reaction kettle, add 100 parts of styrene, 5 parts of divinylbenzene, 1 part of hexafluorobutyl acrylate, and 20 parts of liquid wax in parts by weight, react at 80°C for 6 hours, then heat up to 85°C for reaction 2h, then raise the temperature to 95°C and react for 6h to end the reaction; control the degree of cross-linking at 15, the porosity to 30%, and react to form polymerized white balls. After drying, extract the liquid wax and dry it for later use;

[0054] 2). Chlorination reaction:

[0055] Add chlorine gas to the polymerized white balls obtained in step 1) to carry out chlorination reaction, the reaction temperature is 15 ° C, the reaction is protected from light, the middle sampling is detected, and the reaction is stopped when the chlorine content reaches 20%;

[0056] 3).Sulfonation reaction

[0057] The product obtained in step 2) is sulfonated with an excessive concentration of 90% sulfuric acid, and the temp...

Embodiment 2

[0059] Polymerization reaction crosslinking degree is controlled at 30%, other is the same as embodiment 1. The resulting product number is KRB-2.

Embodiment 3

[0061] Polymerization reaction crosslinking degree is controlled at 22.5%, other is the same as embodiment 1. The resulting product number was KRB-3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a high-temperature-resistant maleic anhydride (MAH) resin catalyst. The resin catalyst is a high-temperature-resistant strong acid cation catalyzed resin obtained by chlorinating fluorine-containing white balls obtained by copolymerizing an acrylic acid fluorine-containing monomer which has the crosslinking degree 15-30 percent and serves as a third monomer, and performing shallow sulfonation. The high-temperature-resistant MAH resin catalyst has a good catalytic effect in an MAH esterification reaction, high high-temperature resistance and long service life, and can be used at high temperature 100-140 DEG C. The invention further provides a preparation method of the catalyst.

Description

technical field [0001] The invention relates to a maleic anhydride resin catalyst and a preparation method thereof, in particular to a high-temperature resistant maleic anhydride resin catalyst and a preparation method thereof. Background technique [0002] Dimethyl maleate is commonly known as dimethyl maleate (DMM). Copolymers of DMM and other substances can be made into a variety of coatings, adhesives, optical materials, and anti-shrinkage materials with special properties and uses. Finishing agent, etc. Therefore, the demand for DMM at home and abroad is also increasing. The traditional method of producing DMM is to use maleic anhydride as raw material, and carry out esterification reaction with methanol under the catalysis of sulfuric acid. Although this production process has high catalytic activity and low price, there are many side reactions and the product is easy to isomerize. Fushun Petrochemical Research Institute (FRIPP) has successfully developed maleic anhy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J31/10C07C69/60C07C67/08C08F212/08C08F212/36C08F220/22C08F2/44C08F8/36C08J9/28
Inventor 刘文飞王金明张勇毛进池
Owner KAIRUI ENVIRONMENTAL PROTECTION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap