Aqueous expansion-preventing transparent primer of medium-density fiber board as well as preparation method and application thereof

A transparent primer, water-based technology, applied in polyurea/polyurethane coatings, special surfaces, devices for coating liquids on surfaces, etc., to improve efficiency, improve the problem of tendon swelling, and improve the effect of leveling and wettability

Active Publication Date: 2012-06-27
深圳市雷巴环保材料有限公司
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem of rib expansion when MDF is coated with existing water-based paints, the primary purpose of the present invention is to provide a water-based anti-swelling rib transparent primer for MDF. White primer coating or solid color primer coating can avoid the occurrence of tendon expansion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous expansion-preventing transparent primer of medium-density fiber board as well as preparation method and application thereof
  • Aqueous expansion-preventing transparent primer of medium-density fiber board as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A preparation method of water-based anti-expansion tendon transparent primer for MDF, comprising the following steps:

[0039] (1) 68 parts of water-based acrylic resin (501BT of Guangzhou Kangzheng Polymer Material Technology Co., Ltd., the glass transition temperature is -10-20 ° C, and the solid content is 55%) and 16 parts of water-based anti-swelling tendon resin (Guangzhou Kangzheng Polymer Material Technology Co., Ltd. XT 1106) of Polymer Materials Technology Co., Ltd. was mixed, and 10.4 parts of water were added under stirring at 400r / min, and mixed for 18min;

[0040] (2) Then add 1 part of zinc stearate, 0.5 part of calcium stearate, 1 part of butanediol, 1.5 parts of alcohol ester-12, 0.5 part of SA-100N (Shanghai Jason Trading Co., Ltd.), 0.5 part of BYK 044 (BYK company), mixed 32min under 600r / min;

[0041] (3) Adjust the rotating speed to 100r / min, add 0.6 parts of hydroxyethyl cellulose and stir for 6 minutes to obtain a water-based anti-swelling tendo...

Embodiment 2

[0044] A preparation method of water-based anti-expansion tendon transparent primer for MDF, comprising the following steps:

[0045] (1) 65 parts of water-based acrylic resin (501BT of Guangzhou Kangzheng Polymer Material Technology Co., Ltd., the glass transition temperature is -10-20 ° C, and the solid content is 55%) and 16 parts of water-based anti-swelling tendon resin (Guangzhou Kangzheng Polymer Material Technology Co., Ltd. XT 1106) of Polymer Materials Technology Co., Ltd. was mixed, and 14.2 parts of water were added under stirring at 400r / min, and mixed for 20min;

[0046] (2) Then add 1 part of zinc stearate, 2 parts of butanediol, 0.2 part of SA-100N (Shanghai Jason Trading Co., Ltd.), 0.4 part of mineral oil, 0.4 part of silicone oil, and mix at 600r / min for 35min;

[0047] (3) Adjust the rotating speed to 100r / min, add 0.8 parts of hydroxyethyl cellulose and stir for 8 minutes to obtain a water-based anti-swelling tendon transparent primer for MDF;

[0048] Sa...

Embodiment 3

[0050] A preparation method of water-based anti-expansion tendon transparent primer for MDF, comprising the following steps:

[0051] (1) 70 parts of water-based acrylic resin (501BT of Guangzhou Kangzheng Polymer Material Technology Co., Ltd., the glass transition temperature is -10-20 ° C, and the solid content is 55%) and 15 parts of water-based anti-swelling tendon resin (Guangzhou Kangzheng Polymer Material Technology Co., Ltd. XT 1106) of Polymer Materials Technology Co., Ltd. was mixed, and 11.6 parts of water were added under stirring at 400r / min, and mixed for 18min;

[0052] (2) Then add 0.5 part of calcium stearate, 2 parts of alcohol ester-12, 0.1 part of SA-100N (Shanghai Jason Trading Co., Ltd.), 0.3 part of mineral oil, and mix at 600r / min for 30min;

[0053] (3) Adjust the rotating speed to 100r / min, add 0.5 parts of hydroxyethyl cellulose and stir for 5 minutes to obtain a water-based anti-swelling tendon transparent primer for MDF;

[0054] Said parts are pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
acid valueaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses an aqueous expansion-preventing transparent primer of a medium-density fiber board as well as a preparation method and application thereof. The aqueous expansion-preventing transparent primer of the medium-density fiber board is prepared from 65-70 parts of aqueous acrylic resin, 15-16 parts of aqueous expansion-preventing resin, 0.5-1.5 parts of grinding auxiliary agent, 2-2.5 parts of film-forming auxiliary agent, 0.1-0.5 part of flatting agent, 0.3-0.8 part of defoaming agent, 0.5-0.8 part of thickening agent and 10.4-11.6 parts of water. By using the aqueous expansion-preventing transparent primer of the medium-density fiber board, the drying and grinding performances are guaranteed, and the expansion phenomenon is not generated after the aqueous expansion-preventing transparent primer is coated on the medium-density fiber board; the aqueous primer is safe and environmentally-friendly, and has efficient sealing performance; and the expansion effect of the wood fiber is eliminated by just requiring one working procedure of spray-coating the aqueous expansion-preventing transparent primer of the medium-density fiber board during the primer treatment of the medium-density fiber board, thus the working procedure is simplified, and the efficiency of grinding personnel is improved.

Description

technical field [0001] The invention relates to a water-based anti-swelling tendon transparent primer for medium-density fiberboards and a preparation method and application thereof. The primer can be used for bottom coating of medium-density fiberboards. Background technique [0002] Wood swelling, or wood grain protrusion, is a common phenomenon in water-based wood paint coating. The mechanism of wood swelling is: wood needs to be cut and sharply cut during processing, which will inevitably cut or destroy wood fibers. Integrity, when the fibers of the wood are exposed, the wood fibers act like straws, drawing moisture into the wood, causing the wood fibers to swell and protrude from the wood surface. [0003] Medium density fiberboard (hereinafter referred to as medium density fiberboard) is a man-made board made of wood fiber or other plant fiber, which is crushed, fiber separated, dried, and then added with an applicable adhesive, and then hot-pressed. Therefore, the su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D175/14C09D7/06C09D7/12B05D7/08B05D5/06C09D7/47
Inventor 曾靖彭成镜孙涛
Owner 深圳市雷巴环保材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products