Resource-conserving type gray plastic foaming polymer composite material and preparation method thereof

A foaming polymer and resource-saving technology, which is applied to resource-saving gray plastic foamed polymer composite materials and the preparation of the above-mentioned composite materials, can solve problems such as difficulties in market promotion, small application range, and large product proportion. Achieve the effects of protecting human health, easy temperature adjustment, and high economic added value

Inactive Publication Date: 2012-08-01
赵芳
View PDF6 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Use thermoplastics PE, PVC and fly ash to mix, and produce floor and other profiles through hot extrusion process. Although this product relatively improves the utilization value of fly ash, the product has a large proportion, high cost, small application range, and market promotion. very difficult to use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A resource-saving gray plastic foamed polymer composite material, the components of which are:

[0028] Thermoplastic PVC 20

[0029] Fly Ash 80

[0030] Aluminate coupling agent 2.5

[0031] Paraffin 2

[0032] Calcium stearate 2

[0033] ACR530—301 4, 5

[0034] Composite blowing agent CU200 2

[0035] Foam regulator HL175S 1.5

[0036] Calcium zinc stabilizer 4.5

[0037] Epoxidized soybean oil 2

[0038] The preparation method of the above-mentioned gray plastic foamed polymer composite material, its specific steps are: (1), prepare raw materials according to the above-mentioned weight ratio; Drying treatment; (3), put the coupling agent, internal and external lubricants into the high mixer and fully mix with the filling agent, and coat and modify the fly ash. The mixing time is 3 to 5 minutes at 120 ° C; (4 ), put the thermoplastic PVC into the high-speed mixer, fully mix and coat with the composite stabilizer and plasticizing accelerator, and mix the ...

Embodiment 2

[0039] A resource-saving gray plastic foamed polymer composite material, the components of which are:

[0040] Thermoplastic PVC 50

[0041] Fly Ash 50

[0042] Silane coupling agent 1

[0043] Polyethylene wax 0.8

[0044] Stearic acid 0.8

[0045]ACR530—201 3.5

[0046] Composite blowing agent C-2 1

[0047] Foam regulator zinc oxide 0.7

[0048] Calcium zinc stabilizer 3

[0049] Epoxidized soybean oil 1

[0050] The preparation method of the above-mentioned gray plastic foamed polymer composite material, its specific steps are:

[0051] (1), prepare raw material by above-mentioned proportioning by weight;

[0052] (2) Put the fly ash into the high temperature mixer at 120 degrees for dehydration and drying;

[0053] (3) Put the coupling agent, internal and external lubricants into the high-mixer and fully mix them with the filling agent to coat and modify the fly ash. The mixing time is 3 to 5 minutes at 120°C;

[0054] (4) Put the thermoplastic PVC into th...

Embodiment 3

[0055] A resource-saving gray plastic foamed polymer composite material, the components of which are:

[0056] Thermoplastic PVC 95

[0057] fly ash 5

[0058] Aluminate coupling agent 0.5

[0059] Paraffin 0.5

[0060] Calcium stearate 0.5

[0061] ACR530—301 2.5

[0062] Composite blowing agent CU200 0.7

[0063] Foam regulator HL175S 0.5

[0064] Calcium zinc stabilizer 2

[0065] Epoxidized soybean oil 0.5

[0066] The preparation method of the above-mentioned gray plastic foamed polymer composite material, its specific steps are: (1), prepare raw materials according to the above-mentioned weight ratio;

[0067] (2) Put the fly ash into the high temperature mixer at 120 degrees for dehydration and drying;

[0068] (3) Put the coupling agent, internal and external lubricants into the high-mixer and fully mix them with the filling agent to coat and modify the fly ash. The mixing time is 3 to 5 minutes at 120°C;

[0069] (4) Put the thermoplastic PVC into...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of building materials, and particularly relates to a resource-conserving type gray plastic foaming polymer composite material. The invention also relates to a preparation method of the composite material. The invention has the technical scheme that the resource-conserving type gray plastic foaming polymer composite material comprises thermoplastic plastic polyvinyl chloride (PVC), filler coal ash, an auxiliary heat stabilizer, a coupling agent, a compound stabilizer, an inside and outside lubricating agent, a plasticizing accelerating agent, a general foaming agent and a foaming regulator. The resource-conserving type gray plastic foaming polymer composite material can be used for utilizing the coal ash with a high added-value in a reclamation way, thus not only saving a great deal of calcium carbonate and timber resources, but also reducing environmental pollution and protecting the human health.

Description

technical field [0001] The invention belongs to the field of building materials, in particular to a resource-saving gray plastic foamed polymer composite material. The present invention also relates to a method for preparing the above-mentioned composite material. Background technique [0002] Fly ash is the largest single emission source of industrial solid waste in my country. For many years, the fly ash of large, medium and small thermal power plants in China has not been efficiently utilized. In the past, traditional storage, burial and other disposal methods have caused serious damage to the environment and brought great harm to public health. At present, my country's fly ash is mainly used to produce concrete, fly ash bricks, cement and other products with low technical content and low added value, and the utilization rate and utilization efficiency are relatively low. Someone recently invented "a formula and preparation method of an environmentally friendly porcelai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/06C08K9/10C08K3/36C08K3/22
Inventor 赵芳
Owner 赵芳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap