Inorganic gelatinous active carbon filter core and preparation method thereof
An activated carbon filter element and inorganic gelling technology, applied in separation methods, chemical instruments and methods, filtration separation, etc., to achieve good water permeability, good market prospects, and wide application range
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] 42.5R ordinary Portland cement and coconut shell activated carbon particles (10-20 mesh) are used to prepare inorganic gelling activated carbon filter elements. The raw material ratio is as follows: activated carbon particles 60 wt%, Portland cement 40 wt%.
[0024] The preparation steps are:
[0025] (1) Ingredients: Weigh 240g activated carbon particles and 160g cement in proportion and mix them evenly.
[0026] (2) Coated granules: spray water while stirring until the cement is all wrapped on the surface of the activated carbon granules and can be kneaded into a mass by hand.
[0027] (3) Granulation: Pass all the above-mentioned wrapped particles through an 8-mesh sieve to prevent agglomeration.
[0028] (4) Injection molding: Put the activated carbon particles into the mold and vibrate and compact.
[0029] (5) Quiet curing demoulding: After the sample is formed, it is placed in a room for 24 hours and demoulded.
[0030] (6) Steaming: Put it in an autoclave at 195°C for more ...
Embodiment 2
[0033] 42.4R ordinary Portland cement and coconut shell activated carbon particles (20-60 mesh) are used to prepare inorganic gelling activated carbon filter elements. The raw materials are as follows: activated carbon particles 80 wt%, Portland cement 20 wt%.
[0034] The preparation steps are:
[0035] (1) Ingredients: Weigh 320g of activated carbon particles and 80g of cement in proportion and mix them evenly.
[0036] (2) Coated granules: spray water while stirring until the cement is all wrapped on the surface of the activated carbon granules and can be kneaded into a mass by hand.
[0037] (3) Granulation: Pass all the above-mentioned wrapped particles through an 8-mesh sieve to prevent agglomeration.
[0038] (4) Injection molding: Put the activated carbon particles into the mold and vibrate and compact.
[0039] (5) Quiet curing demoulding: After the sample is formed, it is placed in a room for 24 hours and demoulded.
[0040] (6) Steaming: Put it in an autoclave at 195°C for 9 ho...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
iodine adsorption value | aaaaa | aaaaa |
compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com