A crystallizer and amorphous technology, applied in the field of crystallizers for the production of amorphous alloys, can solve problems such as immature structure and parameters, failure of various water cooling structures, lack of cooling structures, etc., to achieve uniform cooling in the axial direction and improve precision , high cooling efficiency

Active Publication Date: 2014-01-15
QINGDAO YUNLU ADVANCED MATERIALS TECH CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The immature structure and parameters of the existing domestic and foreign crystallizers, and the diversification of the cooling structure make the experiment of preparing amorphous alloys unscientific, resulting in the failure of various water-cooling structures, but summing up its experience, the structure and design of the crystallizer The key to mastering the principle lies in the heat transfer efficiency and working precision of the crystallizer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Amorphous crystallizer
  • Amorphous crystallizer
  • Amorphous crystallizer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] figure 1 It is a front sectional view of an embodiment of the present invention. 1 is the rotating main shaft, 2 is the end cover, 3 is the copper sleeve support, 4 is the flow regulating rod, 5 is the chrome-zirconium copper sleeve, 6 is the screw plug, 7 is the screw plug, 8 is the twisting taper pin, 9 is the rotating main shaft Deep hole, 10 is the second radial through hole of the rotating spindle, 11 is the first radial through hole for supporting the copper sleeve, 12 is the second axial through hole for supporting the copper sleeve, 13 is the first axial through hole for the copper sleeve, 14 For sealing ring, 15 is the center of the rotating main shaft, and 16 is the end face groove supported by the copper sleeve. Both the copper sheath 5 and the copper sheath support 3 are annular, and there is a copper sheath support 3 on each of the left and right sides of the copper sheath 5 . The end cover 2 is connected to the rotating main shaft 1 and the copper sleeve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a crystallizer which is mainly used for preparing amorphous alloy. The amorphous crystallizer is composed of a copper sleeve 5, a copper sleeve support 3 and a rotary spindle 1; when the crystallizer works, cold water flows in from a water inlet end of the rotary spindle and flows into the copper sleeve 5 along the pore channels in the rotary spindle 1 and the copper sleeve support 3; the cold water absorbs the heat of molten steel transferred from the outer surface of the copper sleeve; and then the hot water returns to a water outlet end in the rotary spindle from the copper sleeve support 3 at the other end of the copper sleeve 5 along the path opposite to the cold water and flows out so as to circularly cool the molten steel. The crystallizer provided by the invention has the advantages that: the cooling efficiency is high, the surface temperature of the copper sleeve is uniform, a water flow dead angle does not exist in the copper sleeve, the axial cooling of the copper sleeve is uniform, the mechanical performance is good, and the working precision is high; and the heat transfer effect of applying the amorphous crystallizer to cool the molten steel is guaranteed.

Description

Technical field: [0001] The invention relates to a crystallizer, in particular to a crystallizer for producing amorphous alloy. Background technique: [0002] Amorphous alloys are solidified by ultra-rapid cooling. When the alloy is solidified, the atoms do not have time to arrange and crystallize in an orderly manner. The obtained solid alloy has a long-range disordered structure, and there are no grains and grain boundaries of the crystalline alloy. [0003] The production technology of amorphous alloy is to pour 1300 ℃ alloy steel on the high-speed rotating water-cooled copper sleeve, and instantly cool it to below 200 ℃ to form amorphous alloy. [0004] The immature structure and parameters of the existing domestic and foreign crystallizers, and the diversification of the cooling structure make the experiment of preparing amorphous alloys unscientific, resulting in the failure of various water-cooling structures, but summing up its experience, the structure and design of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/06
Inventor 李晓雨石晓敬秦振武李庆华张连学姜宁
Owner QINGDAO YUNLU ADVANCED MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap