High-temperature corrosion-resistant phosphating solution

A corrosion-resistant, phosphating technology, applied in the direction of metal material coating process, etc., can solve the problems of insufficient adhesion of phosphating film, limited material range, weak corrosion resistance, etc., and achieves good blackness and material range. Wide and strong adhesion

Inactive Publication Date: 2012-12-12
BENGBU FUWOTE WHEEL MFG TECH
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing phosphating solution has a limited range of materials for workpieces, and the formed phosphating film has insufficient adhesion, poor corrosion resistance, and poor stability in high-temperature environments.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] A high-temperature corrosion-resistant phosphating solution, a mixed solution prepared from the following components, the weight of each component in each liter of mixed solution is:

[0030] 80% phosphoric acid 425g

[0031] Zinc oxide 122g

[0032] Sodium molybdate 6g

[0033] Citric acid 12.5g

[0034] Zinc nitrate 120g

[0035] Nitric acid 5g

[0036] Nickel nitrate 5g

[0037] Chromic acid 2.2g

[0038] Polyvinyl alcohol 3 g

[0039] Sodium hydroxymethylcellulose 2 g

[0040] The balance is water.

[0041] When working: Prepare the above phosphating solution stock solution and water at a ratio of 1:15 to make a working solution.

[0042] First, pour water into the phosphating tank to 60% of the effective volume of the phosphating tank, weigh the required amount of the phosphating solution of this embodiment and pour it into the phosphating tank to fully stir to make a working solution, and adjust the process range of the working solution to the total acidi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a high-temperature corrosion-resistant phosphating solution. The phosphating solution is a mixture comprising the following components by weight in per liter mixture: 320-330g of 80% phosphoric acid, 120-125g of zinc oxide, 5-7g of sodium molybdate, 12-13g of citric acid, 100-150g of zinc nitrate, 4-6g of nitric acid, 4-6g of nickel nitrate, 2.0-2.5g of chromic acid, and the balance of water. The phosphating solution provided by the invention can treat a variety of metal workpiece materials with a short working time. The phosphating film formed on the surface of the workpieces is thick and dense and has the characteristics of good adhesion, good blackness, high corrosion resistance and high stability. The phosphating solution can be widely used for motors, gears, a variety of high strength carbon steels, alloy steel works and the like, and is suitable to be used in a high temperature environment with a stable operation.

Description

technical field [0001] The invention relates to the field of metal surface pretreatment, in particular to a high-temperature corrosion-resistant phosphating solution. Background technique [0002] Phosphating is a commonly used pre-treatment technology. The main purpose of phosphating is to provide protection for the base metal and prevent the metal from being corroded to a certain extent; it is used as a primer before painting to improve the adhesion and corrosion resistance of the paint film layer. ; Anti-friction lubrication in metal cold working process. The material range of workpieces treated with the existing phosphating solution is not wide, the adhesion of the formed phosphating film is not enough, the corrosion resistance is not strong, and the stability in high temperature environment is poor. Contents of the invention [0003] The invention provides a high-temperature corrosion-resistant phosphating solution. The metal workpieces treated by the phosphating...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/43
Inventor 年君
Owner BENGBU FUWOTE WHEEL MFG TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap