Method for shaping and extracting ashing silk fabric cultural relics on unearthed sites

A technology for silk fabrics and cultural relics, which is applied in the field of setting and extraction of grayed silk fabric cultural relics unearthed, which can solve the problems of difficult extraction, ashing, carbonization, and serious decay, and achieve the effect of improving mechanical strength and increasing toughness

Inactive Publication Date: 2012-12-12
荆州文物保护中心
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the particularity of the material, the silk cultural relics were extremely decayed when they were unearthed, and even appeared in a state of serious ash and carbonization, making it difficult to completely extract them, which greatly affected the subsequent protection, research and display, and also lost the cultural relics. Fundamental value, causing irreparable loss

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for shaping and extracting ashing silk fabric cultural relics on unearthed sites
  • Method for shaping and extracting ashing silk fabric cultural relics on unearthed sites
  • Method for shaping and extracting ashing silk fabric cultural relics on unearthed sites

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Example 1: The stereotypes and extraction of the unearthed site of the ashesed silk fabric cultural relics unearthed from the tomb of Zhang Anshi's family in Fengqiyuan, Xi'an;

[0022] Firstly, 5% benzoic acid and 95% dehydrated alcohol are mixed and prepared into benzoic acid dehydrated alcohol solution by weight percentage, then benzoic acid dehydrated alcohol solution is packed in the small sprayer; The benzoic acid dehydrated alcohol solution of benzoic acid The quality is 99.5%, and the absolute ethanol is 99.7%. At the excavation site of the cultural relics, use a sprayer to spray the benzoic acid absolute ethanol solution on the surface of the silk fabric cultural relics that has appeared. The process of spraying the benzoic acid absolute ethanol solution should be repeated several times to make the benzoic acid absolute ethanol solution completely soak the silk fabric cultural relics . After spraying the benzoic acid absolute ethanol solution, wait for 3-5 hou...

Embodiment 2

[0025] Example 2: The stereotypes and extraction of the Warring States ashed silk fabric cultural relics unearthed from Baling Mountain, Jingzhou City, Hubei Province;

[0026] Firstly, 5% benzoic acid and 95% dehydrated alcohol are mixed and prepared into benzoic acid dehydrated alcohol solution by weight percentage, then benzoic acid dehydrated alcohol solution is packed in the small sprayer; The benzoic acid dehydrated alcohol solution of benzoic acid The quality is 99.5%, and the absolute ethanol is 99.7%. At the excavation site of the cultural relics, use a sprayer to spray the benzoic acid absolute ethanol solution on the surface of the silk fabric cultural relics that has appeared. The process of spraying the benzoic acid absolute ethanol solution should be repeated several times to make the benzoic acid absolute ethanol solution completely soak the silk fabric cultural relics . After spraying the benzoic acid absolute ethanol solution, wait for 3-5 hours to completely...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for shaping and extracting ashing silk fabric cultural relics on unearthed sites, and belongs to the technical field of ancient silk fabric cultural relic protection. The method includes mixing 5% of benzoic acids and 95% of absolute ethyl alcohol to be prepared into a benzoic acid absolute ethyl alcohol solution, and spraying the solution onto surfaces of the silk fabric cultural relics, so that shaping and intensity enhancing effects are provided for the silk fabric cultural relics; peeling the silk fabric cultural relics with a bamboo knife, so that the loss of messages and the like of organization structures and influences on values of the silk fabric cultural relics caused by the moving or scattering of the silk fabric cultural relics due to the severe ashing degree are avoided; the benzoic acid absolute ethyl alcohol solution utilizes the absolute ethyl alcohol as a solvent which can be dissolved with water in any proportion, and the method is applicable to the shaping and the extracting of the silk fabric cultural relics of ashed and carbonized states in various moisture content conditions.

Description

technical field [0001] The invention relates to a method for shaping and extracting grayed silk cultural relics unearthed on site, and belongs to the technical field of ancient silk cultural relics protection. Background technique [0002] Silk cultural relics are extremely important and precious historical materials for studying the political, economic, cultural, artistic and scientific and technological conditions of ancient my country, and have extremely important archaeological, scientific and artistic values. Due to the particularity of the material, the silk cultural relics were extremely decayed when they were unearthed, and even appeared in a state of serious ash and carbonization, making it difficult to completely extract them, which greatly affected the subsequent protection, research and display, and also lost the cultural relics. essential value, resulting in irreparable loss. Although the visual effect of ashesed silk fabrics is not good for the audience when t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/188D06M101/10
Inventor 吴顺清魏彦飞陈光利
Owner 荆州文物保护中心
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com