Preparation method of columnar potassium hexatitanate

A potassium hexatitanate and columnar technology is applied in the field of preparation of columnar potassium hexatitanate, and can solve the problems of harsh boiling conditions of deionized water, difficulty in separation of potassium hexatitanate, small aspect ratio of potassium hexatitanate, and the like, Achieve the effect of low cost, large aspect ratio and improved purity

Inactive Publication Date: 2014-10-01
PANZHIHUA UNIV
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 1. It can be seen from the content of the patent that the potassium hexatitanate produced by this method has a small aspect ratio and a low yield;
[0006] 2. There are titanium dioxide impurities in the produced potassium hexatitanate, and it is not easy to separate the potassium hexatitanate
The main disadvantages of this method are: 1. The product production cycle is long; 2. The boiling conditions in deionized water are too harsh

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of columnar potassium hexatitanate
  • Preparation method of columnar potassium hexatitanate
  • Preparation method of columnar potassium hexatitanate

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] The preparation method of columnar potassium hexatitanate of the present invention comprises the following steps:

[0025] a. Put -100 mesh titanium-containing raw materials and potassium-containing raw materials according to TiO 2 :K 2 The molar ratio of O=4~7 is mixed evenly;

[0026] b. Sintering the uniformly mixed material in step a at a temperature of 1100-1300°C for 1-4 hours to fully react the material;

[0027] c. Rapidly cool the sintered material in step b, then fully dissociate the cooled material with water under a constant temperature environment of 60-80°C, and finally filter and dry to obtain the columnar potassium hexatitanate product.

[0028] The particle size of the raw material of the invention is -100 mesh, so that the bulk volumes of the titanium-containing raw material and the potassium-containing raw material are basically the same, which is conducive to uniform mixing and sufficient contact of the raw materials. Raw material according to TiO...

Embodiment 1

[0036] Mix metatitanic acid (water content 20%) and -100 mesh potassium hydroxide according to TiO 2 :K 2 Weigh the molar ratio of O=5.5, and mix the two evenly;

[0037] Put the above-mentioned mixed raw materials into a crucible of appropriate size, and put the crucible into a high-temperature box-type resistance furnace at 1150 ° C, and stay for 3 hours;

[0038]The above-mentioned sintered product is taken out, and immediately put into a water container to cool;

[0039] After the cooling of the product is completed, take the product out of the water, put the product in the crucible into a beaker containing 400ml of water, put the beaker into a water bath set at a temperature of 70°C, and stir the product in the beaker to make the whisker product Full dissociation, the dissociation time is 2h;

[0040] After the above-mentioned dissociated products are suction-filtered, put them in an oven at 90°C and dry them to obtain the finished product.

[0041] See the SEM figure...

Embodiment 2

[0044] Put -100 mesh anatase titanium dioxide and potassium hydroxide in accordance with TiO 2 :K 2 Weigh the molar ratio of O=5.5, and mix the two evenly;

[0045] Put the above-mentioned mixed raw materials into a crucible of appropriate size, and put the crucible into a high-temperature box-type resistance furnace at 1150 ° C, and stay for 3 hours;

[0046] The above-mentioned sintered product is taken out, and immediately put into a water container to cool;

[0047] After the cooling of the product is completed, take the product out of the water, put the product in the crucible into a beaker containing 400ml of water, put the beaker into a water bath set at a temperature of 70°C, and stir the product in the beaker to make the whisker product Full dissociation, the dissociation time is 2h;

[0048] After the above-mentioned dissociated products are suction-filtered, put them in an oven at 90°C and dry them to obtain the finished product.

[0049] See the SEM image and X...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
aspect ratioaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of columnar hexagonal potassium titanate, which belongs to the field of the chemical industry. The method comprises the steps of: a, uniformly mixing a -100 mesh titaniferous containing material and a potassium containing material according to a molar ratio of TiO2:K2O=4-7; b, placing the material mixed uniformly in the step a in an environment at 1100-1300 DEG C for sintering for 1-4 hours for adequate reaction of the material; and c, quickly cooling the sintered material in the step b, then adequately dissociating the cooled material by water at a constant temperature of 60-80 DEG C, and finally filtering and drying to obtain a columnar hexagonal potassium titanate product. The method provided by the invention is simple in process flow, easy to operate, low in cost and high in yield, and the prepared columnar hexagonal potassium titanate is large in draw ratio and high in purity, and is suitable for industrial production.

Description

technical field [0001] The invention belongs to the field of chemical industry, and in particular relates to a preparation method of columnar potassium hexatitanate. Background technique [0002] Potassium titanate whiskers can be expressed as K 2 O nTiO 2 , n can be 2, 4, 6 and 8, representing potassium dititanate, potassium tetratitanate, potassium hexatitanate and potassium octatitanate respectively. In 1994, Professor Huang Jifen introduced in the article "Inorganic Reinforcing Fiber I Potassium Titanate Fiber" published in "Salt Lake Research" (see P69-75): Potassium hexatitanate (K 2 Ti 6 o 13 ), showing a tunnel structure, composed of TiO 6 Octahedrons are connected by coplanarity and common edges to form a crystal with a wind tunnel structure. K ions occupy the wind tunnel, and the wind tunnel axis is parallel to the fiber axis. The K ions in potassium hexatitanate are wrapped in this wind tunnel-like structure to isolate it from the environment. Even in soluti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G23/00
Inventor 张树立王本菊刘黔蜀王海波孙青竹罗燕白桂华
Owner PANZHIHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com