A technology of azo dyes and azo compounds, applied in organic dyes, dyeing methods, textiles and papermaking, etc., can solve the problems of deep dyeing, insufficient lifting power, poor level dyeing, poor fastness, etc., and achieve excellent sublimation fastness degree, good affinity, good dyeing effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0064] Example 1
[0065] 14.9 g of the dye of formula (Ia) 10.1 g of sodium lignosulfonate was mixed with 75 ml of water, and then ground and dispersed with a grinder to obtain an aqueous dye product. 1.0 g of this product was dyed with 10.0 g of polyester fiber at pH 4.5 and 130°C for 60 minutes, and then washed, rinsed, and dried to obtain a bright navy blue dyed product with excellent washing and various fastness properties.
[0066]
Example Embodiment
[0067] Example 2
[0068] Add 15.0 g of the dye of formula (Ib), 13.2 g of the dye of formula (IIa), 15.0 g of the dye of formula (IIIa), 6.8 g of dye of formula (Va), 50 g of sodium lignosulfonate, and 300 ml of water After mixing, use a grinder to grind and disperse, and spray dry (inlet temperature is 130°C, outlet temperature is 60°C) to obtain 100 grams of finished product. 0.4g of this product was dyed with 10.0g of polyester fiber at pH 4.5 and 130°C for 60 minutes, then washed, rinsed, and dried to obtain bright black dyed products with excellent fastness properties.
[0069]
[0070]
Example Embodiment
[0071] Example 3
[0072] Add 11.5 g of the dye of formula (Ib), 11.2 g of the dye of formula (IIa), 13.5 g of the dye of formula (IIIa), 5.8 g of dye of formula (Va), 98 g of sodium lignosulfonate to 450 ml of water After mixing, the dye mixture was prepared according to the method of Example 2, and then the polyester fiber was dyed according to the method of Example 2 to obtain bright black dyed products with excellent fastness properties. .
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap